Thermoluminescence characterization of Ag-doped Li2 B4 O7 single crystal materials.

In this study, the thermoluminescence (TL) characteristics of Ag-doped and undoped lithium tetraborate (Li2 B4 O7 , LTB) materials, grown using the Czochralski method, were reported. The TL properties of LTB:Ag, such as glow curve structure, dose response, fading and reproducibility, were investigated. The glow curve of the Li2 B4 O7 :Ag single crystal consists of four peaks located at approximately 75, 130, 190 and 275°C; in undoped LTB, the single crystal shows a broad glow curve with peaks at 65, 90, 125, 160 and 190°C using a heating rate of 5°C/s in the 50-350°C temperature region. The high temperature peak of Ag-doped sample at 275°C has a nonlinear dose response within the range from 33 mGy to 9 Gy. There is a linear response in the range of 33-800 mGy; after which, a sublinear region appears up to 9 Gy for Ag-doped LTB single crystal. For undoped single crystal, the dose response is supralinear for low doses and linear for the region between 1 and 9 Gy. The thermal fading ratio of the undoped material is almost 60% for the high temperature peak after 7 days. Ag-doped LTB single crystal exhibits different behaviour over a period of 7 days.

Optical spectroscopy of the Ce-doped multicomponent garnets.

Here, we report our results referring to the preparation of Ce doped Y2.22MgGa2Al2SiO12, Y1.93MgAl4SiO12 and Y2.22Gd0.75Ga2Al3O12 using solid state reaction at high temperature. Several complementary methods (i.e. powder x-ray diffraction (XRPD), energy dispersive analysis of X-rays (EDX), scanning electron microscopy (SEM) and Fourier transforms infrared spectroscopy (FTIR)) were studied to examine the effects of the synthesis procedure on the morphology and structure. XRD analyses revealed that all compounds include yttrium aluminate phase with garnet structure. Cathodoluminescence (CL), radioluminescence (RL) and photoluminescence (PL) measurements were carried out for clarification of relationship between host lattice defects and the spectral luminescence emissions. Luminescence emission of phosphors is peaked at 530nm assigned to 5d-4f transitions of the dopant Ce(3+) ions with a broad emission band in 400-700nm range. Under electron irradiation, the emission spectrum of Ce doped (YGd)3Ga2Al3O12 is well defined and has a characteristic fairly narrow and sharp emission band peaking at 312nm and 624nm corresponding to transition of (6)P7/2 →(8)S7/2 and (6)GJ→(6)PJ (Gd(3+)), respectively. We suggest some of phosphors might be excellent phototherapy phosphor materials under electron excitation.

Thermoluminescence studies of Nd doped Bi4Ge3O12 crystals irradiated by UV and beta sources.

Thermoluminescence (TL) glow curves of pure and rare earth doped bismuth germanate (BGO) were investigated under UV and beta radiation. The glow curves of pure BGO crystal present different patterns for both kinds of radiation. The TL glow curves of BGO crystals doped with Nd ions are similar to that of pure BGO under UV radiation. The kinetic parameters, kinetic order (b), activation energy (E) and frequency factor (s) of the TL glow curves of pure BGO crystal have been determined by peak shape method. Activation energies of 3 peaks obtained by PS were found to be 1.81, 1.15 and 1.78, respectively.

Visible to infrared low temperature photoluminescence of rare earth doped bismuth germanate crystals.

In this paper, the influence of a series of rare earth (Eu, Tm, Nd) and Cr ion doping on the optical properties of BGO was investigated by means of photoluminescence (PL) from visible to IR region in the 10-300K temperature range using different types of detectors, namely, photomultiplier tube (PMT), InGaAs (IGA), and Si. Several samples were investigated having dopants concentrations of 0.3wt%Nd, 0.4wt%Tm, 0.06wt% Cr and 3ppm Eu. The PL spectra of the samples showed different luminescence behaviour which is assigned to the 4f intra shell transition from rare earth ions. The temperature dependence of the PL from rare earth doped BGO crystals is also examined.

Characterisation and luminescence studies of Tm and Na doped magnesium borate phosphors.

In this study, structural and luminescence properties of magnesium borate of the form MgB4O7 doped with Tm and Na were investigated by X-ray diffraction (XRD), Raman spectroscopy and cathodoluminescence (CL). The morphologies of the synthetised compounds exhibit clustered granules and road-like materials. As doping trivalent ions into a host with divalent cations requires charge compensation, this effect is discussed. The CL spectra of undoped MgB4O7 shows a broad band emission centred around 350 nm which is postulated to be produced by self-trapped excitons and some other defects. From the CL emission spectrum, main emission bands centred at 360, 455, 475 nm due to the respective transitions of (1)D2→(3)H6,(1)D2→(3)F4 and (1)G4→(3)H6 suggest the presence of Tm(3+) ion in MgB4O7 lattice site. CL mechanism was proposed to explain the observed phenomena which are valuable in possibility of the developing new luminescent materials for different applications. In addition, the experimental Raman spectrum of doped and undoped MgB4O7 were reported and discussed.

Spectrally resolved luminescence of undoped and Dy3+ doped Na2SO4.

Structural phase transitions influence the luminescence characteristics by modifying the spectra, sensitivity and luminescence efficiency in each phase. This has implications for dosimetric materials both for sensitivity and reproducibility. Previous work with dosemeter materials has not documented effects of different phases on thermoluminescence but Na2SO4 exists in several phases in the temperature range of interest for thermoluminescence dosimetry. Therefore spectrally resolved TL and radiothermoluminescence analyses of undoped and Dy3+ doped Na2SO4 have been performed. Dramatic differences between TL of slow cooled and quenched Na2SO4:Dy are explained in terms of the initial phase of the samples at room temperature. For undoped material the effect of phase conversions during heating shift the wavelengths of the emission bands. A model of Dy in small precipitate phases is considered.

Thermoluminescent spectra of rare earth doped MgB4O7 dosemeters.

This paper presents X ray excited TL spectra of magnesium borate doped with either single rare earth ions Dy or Tm, or co-doped with Dy/Tm, Tm/Mn or Dy/Tb. Intrinsic emission from the host material is in the UV/blue region at approximately 375 nm, with a tail extending to 200 nm. The main dosimetric peak is detected at approximately 180 degrees C but slight differences are noted between the glow peak maxima from the different rare earth ions and there were changes following thermal treatments. The results are discussed according to the interaction between trapping and rare earth sites.