RESUMO
To improve the lifetime of lithium-ion batteries, a detailed understanding of the degradation mechanisms is essential. Nuclear magnetic resonance (NMR) is able to unravel the reversible as well as irreversible transient changes of composition, shape and morphology in a battery cell. Using a newly developed cylindrical battery container free of metallic components in combination with a numerically optimized saddle coil, in operando NMR investigations of battery cells over hundreds of charge/discharge cycles are presented. Alternating with NMR data acquisition, electrochemical impedance spectra (EIS) can be recorded, which enables correlative analysis of the two techniques. Long-run in operando NMR measurements on a Li metal vs. graphite cell reveal the formation and evolution of mossy and dendritic Li microstructures over a period of 1000 h, which illustrates the capabilities of NMR to identify dendrite mitigation strategies in cells operated under realistic conditions.
RESUMO
Electrochemical cells contain electrically conductive components, which causes various problems if such a cell is analyzed during operation in an EPR resonator. The optimum cell design strongly depends on the application and it is necessary to make certain compromises that need to be individually arranged. Rapid prototyping presents a straightforward option to implement a variable cell design that can be easily adapted to changing requirements. In this communication, it is demonstrated that sample containers produced by 3D printing are suitable for EPR applications, with a particular emphasis on electrochemical applications. The housing of a high temperature polymer electrolyte fuel cell (HT-PEFC) with a phosphoric acid doped polybenzimidazole membrane was prepared from polycarbonate by 3D printing. Using a custom glass Dewar, this fuel cell could be operated at temperatures up to 140°C in a standard EPR cavity. The carbon-based gas diffusion layer showed an EPR signal with a characteristic Dysonian line shape, whose evolution could be monitored in-operando in a non-invasive manner.
RESUMO
Using an ultrastable continuous-wave laser at 580 nm we performed spectral hole burning of Eu(3+):Y(2)SiO(5) at a very high spectral resolution. The essential parameters determining the usefulness as a macroscopic frequency reference, linewidth, temperature sensitivity, and long-term stability, were characterized using a H-maser stabilized frequency comb. Spectral holes with a linewidth as low as 6 kHz were observed and the upper limit of the drift of the hole frequency was determined to be 5±3 mHz/s. We discuss the necessary requirements for achieving ultrahigh stability in laser frequency stabilization to these spectral holes.