N-Acetylcysteine-Loaded Magnetic Nanoparticles for Magnetic Resonance Imaging.

Acute respiratory distress syndrome (ARDS) is a life-threatening condition characterized by the rapid onset of lung inflammation Therefore, monitoring the spatial distribution of the drug directly administered to heterogeneously damaged lungs is desirable. In this work, we focus on optimizing the drug N-acetylcysteine (NAC) adsorption on poly-l-lysine-modified magnetic nanoparticles (PLLMNPs) to monitor the drug spatial distribution in the lungs using magnetic resonance imaging (MRI) techniques. The physicochemical characterizations of the samples were conducted in terms of morphology, particle size distributions, surface charge, and magnetic properties followed by the thermogravimetric quantification of NAC coating and cytotoxicity experiments. The sample with the theoretical NAC loading concentration of 0.25 mg/mL was selected as an optimum due to the hydrodynamic nanoparticle size of 154 nm, the surface charge of +32 mV, good stability, and no cytotoxicity. Finally, MRI relaxometry confirmed the suitability of the sample to study the spatial distribution of the drug in vivo using MRI protocols. We showed the prevailing transverse relaxation with high transverse relaxivity values and a high r2(*)/r1 ratio, causing visible hypointensity in the final MRI signal. Furthermore, NAC adsorption significantly affects the relaxation properties of PLLMNPs, which can help monitor drug release in vitro/in vivo.

Development of Positively Charged Poly-L-Lysine Magnetic Nanoparticles as Potential MRI Contrast Agent.

A colloidal solution of magnetic nanoparticles (MNPs) modified with biocompatible positively charged poly-L-lysine (PLL) with an oleate (OL) layer employed as an initial coating was produced as a potential MRI contrast agent. The effect of various PLL/MNPs' mass ratios on the samples' hydrodynamic diameter, zeta potential, and isoelectric point (IEP) was studied by the dynamic light-scattering method. The optimal mass ratio for MNPs' surface coating was 0.5 (sample PLL0.5-OL-MNPs). The average hydrodynamic particle size in the sample of PLL0.5-OL-MNPs was 124.4 ± 1.4 nm, and in the PLL-unmodified nanoparticles, it was 60.9 ± 0.2 nm, indicating that the OL-MNPs' surface became covered by PLL. Next, the typical characteristics of the superparamagnetic behavior were observed in all samples. In addition, the decrease in saturation magnetizations from 66.9 Am2/kg for MNPs to 35.9 and 31.6 Am2/kg for sample OL-MNPs and PLL0.5-OL-MNPs also confirmed successful PLL adsorption. Moreover, we show that both OL-MNPs and PLL0.5-OL-MNPs exhibit excellent MRI relaxivity properties and a very high r2(*)/r1 ratio, which is very desirable in biomedical applications with required MRI contrast enhancement. The PLL coating itself appears to be the crucial factor in enhancing the relaxivity of MNPs in MRI relaxometry.

Targeting of carbonic anhydrase IX-positive cancer cells by glycine-coated superparamagnetic nanoparticles.

Antibody-modified magnetic nanoparticles were prepared to study their cellular uptake in 3D multicellular spheroidal cell cultures. For this purpose, carbonic anhydrase IX specific monoclonal antibody VII/20 was selected to conjugate on the surface of positively charged glycine coated magnetic nanoparticles in a form of a stable magnetic fluid. In this work, glycine-functionalized magnetic nanoparticles were characterized by different methods. X-ray photoelectron analysis confirmed the binding of glycine to the magnetic nanoparticles, and quantification of the glycine coating on the surface of the magnetic nanoparticles was conducted by thermogravimetric analysis. The optimal weight ratio of glycine to magnetic nanoparticles was determined to be 5 showing good colloid stability due to the high surface charge density of protonated glycine coating shown by the great zeta potential (⁓40 mV). The antibody conjugation to the functionalized magnetic nanoparticles was performed at an antibody to magnetic nanoparticles weight ratio equal to 0.5. Applications of antibody-modified magnetic nanoparticles in cancer therapy rely on their ability to specifically target cancer tissues and enter the tumour intracellular space. Here, we show that antibody coupled nanoparticle internalization was triggered by selective binding to tumour cells expressing hypoxic marker carbonic anhydrase IX. Moreover, our results confirmed specific penetration of conjugated nanoparticles into the tumour cell spheroids.

Influence of Dextran Molecular Weight on the Physical Properties of Magnetic Nanoparticles for Hyperthermia and MRI Applications.

Dextran-coated magnetic nanoparticles are promising biocompatible agents in various biomedical applications, including hyperthermia and magnetic resonance imaging (MRI). However, the influence of dextran molecular weight on the physical properties of dextran-coated magnetic nanoparticles has not been described sufficiently. We synthesise magnetite nanoparticles with a dextran coating using a co-precipitation method and study their physical properties as a function of dextran molecular weight. Several different methods are used to determine the size distribution of the particles, including microscopy, dynamic light scattering, differential centrifugal sedimentation and magnetic measurements. The size of the dextran-coated particles increases with increasing dextran molecular weight. We find that the molecular weight of dextran has a significant effect on the particle size, efficiency, magnetic properties and specific absorption rate. Magnetic hyperthermia measurements show that heating is faster for dextran-coated particles with higher molecular weight. The different molecular weights of the coating also significantly affected its MRI relaxation properties, especially the transversal relaxivity r2. Linear regression analysis reveals a statistically significant dependence of r2 on the differential centrifugal sedimentation diameter. This allows the targeted preparation of dextran-coated magnetic nanoparticles with the desired MRI properties. These results will aid the development of functionalised magnetic nanoparticles for hyperthermia and MRI applications.

MRI Relaxivity Changes of the Magnetic Nanoparticles Induced by Different Amino Acid Coatings.

In this study, we analysed the physico-chemical properties of positively charged magnetic fluids consisting of magnetic nanoparticles (MNPs) functionalised by different amino acids (AAs): glycine (Gly), lysine (Lys) and tryptophan (Trp), and the influence of AA-MNP complexes on the MRI relaxivity. We found that the AA coating affects the size of dispersed particles and isoelectric point, as well as the zeta potential of AA-MNPs differently, depending on the AA selected. Moreover, we showed that a change in hydrodynamic diameter results in a change to the relaxivity of AA-MNP complexes. On the one hand, we observed a decrease in the relaxivity values, r1 and r2, with an increase in hydrodynamic diameter (the relaxivity of r1 and r2 were comparable with commercially available contrast agents); on the other hand, we observed an increase in r2* value with an increase in hydrodynamic size. These findings provide an interesting preliminary look at the impact of AA coating on the relaxivity properties of AA-MNP complexes, with a specific application in molecular contrast imaging originating from magnetic nanoparticles and magnetic resonance techniques.

d,l-lysine functionalized Fe3O4 nanoparticles for detection of cancer cells.

Amino-modified magnetic nanoparticles were prepared by direct chemisorption of biocompatible d,l-lysine (DLL) on electrostatically stabilized magnetic nanoparticles with the aim to bind specific antibodies (Ab) able to detect cancer cells. The magnetic nanoparticles prepared by coprecipitation were stabilized in an acidic medium. A full optimization study of amino modification performed by UV/Vis spectroscopy and Dynamic Light Scattering measurement (DLS) confirmed an optimal DLL/Fe3O4 weight ratio of 2. The sample was subjected to complex characterizations using different techniques such as UV/Vis, FTIR and X-ray photoelectron spectroscopies (XPS) together with transmission electron microscopy and size/zeta potential measurements. While FTIR spectroscopy, UV/Vis spectroscopy and XPS confirmed the successful amino modification of Fe3O4 nanoparticles, a characterization using a vibrating sample magnetometer (VSM) indicated superparamagnetic behavior in all the prepared samples, suggesting that the coating process did not significantly affect the size and structure of the Fe3O4 nanoparticles. Magnetic nanoparticles with the optimal DLL content were conjugated with the M75 monoclonal antibody specific to carbonic anhydrase IX (CA IX), which is considered one of the best markers of tumor hypoxia and a prognostic indicator of cancer progression. The results demonstrate that all tested cell lines survived and even proliferated in the presence of amino-modified magnetic nanoparticles. Even the tubulin cytoskeletal structure was not disrupted after the exposure of cells to surface-modified magnetic nanoparticles. In contrast, internalization of the antibody-conjugated magnetic nanoparticles led to abrogation of the formation of long and extended microtubules. Finally, the finding supports the view that the M75 antibody conjugated to nanoparticles mediates their specific uptake and intracellular accumulation and that the antibody conjugated magnetic nanoparticles can be potentially used for the selective growth inhibition of CA IX-expressing cells.