RESUMO
Aim: Resin-modified glass ionomer cement tends to shrink due to polymerization of the resin component. Additionally, they are more prone to syneresis and imbibition during the setting process. This in vitro study evaluates the impact of chitosan, a biopolymer that is, both biomaterial and biocompatible, on the strength of dentin bonding and compares it with ACTIVA Bio-ACTIVE Restorative. The present study was aimed to assess the impact of including chitosan into Fuji II on the shear bond strength between. the restoration material and tooth dentin, in contrast to Bioactiva in permanent teeth. Materials and Methods: A total of 30 premolar teeth were recently extracted. The study involved three distinct sample groups. Group 1 (10 teeth) is the negative control (Fuji II), Group 2 (10 teeth) is the positive control (ACTIVA Bio-ACTIVE Restorative), and Group 3 (10 teeth) is treated with a mixture of Chitosan and Fuji II (CH-Fuji II). Each tooth's buccal and palatal cusps were eliminated to achieve a horizontal surface. Using a periodontal probe, 1.5 mm from the mesial pit to the mesial marginal ridge were removed. Restoration was implemented in all groups following manufacturer directions. Thermocycling the teeth by immersing them in a water bath with temperatures ranging from 5°C to 55°C (± 1-2°C) for 30 s (500 cycles). Each sample was attached to the universal testing machine's jig at a cross-head speed of 1 mm/min. Shear force was used until breakage, and the bond's adhesive strength was then calculated. Statistical analysis using ANOVA with Dunnett's T3 post hoc test. Results were significant at P < 0.05. Results: Statistically significant difference was present between Chitosan and Fuji II and between Chitosan and Activa by reducing the shear bond strength. Conclusions: Addition of chitosan to Fuji II had a negative effect on the shear bond with a significant difference while Activa and Fuji II exhibited favorable shear bond strength.