Growth and NO2-Sensing Properties of Biaxial p-SnO/n-ZnO Heterostructured Nanowires.

Biaxial p-SnO/n-ZnO heterostructured nanowires (average length of 10 µm) were grown onto a glass substrate by thermal evaporation in vacuum. These nanowires had spherical ball tips, and the size of the SnO part increased gradually from the top to the bottom of the nanowire, but the corresponding size of ZnO varied slightly. The Sn-Zn alloy formed in the tips resulted in determined as the catalyst of the growth of the ZnO nanowires. The growth process of the p-SnO/n-ZnO biaxial nanowires is discussed based on vapor-liquid-solid (VLS) based on the subsequent growth process: the VLS catalytic growth of the ZnO nanowire and subsequent epitaxial SnO growth on the sidewall of the pregrown ZnO nanowire. An epitaxial relationship, (001)SnO//(110)ZnO and [110]SnO//[002]ZnO, was observed in the biaxial p-SnO/n-ZnO heterostructured nanowires. The gas-sensing properties of the as-synthesized p-SnO/n-ZnO nanowires were investigated. The results show that the device exhibit a good performance to the ppb-level NO2 at room temperature (25 °C) without light illumination. The detection limit of the p-SnO/n-ZnO sensor to NO2 is 50 ppb. Moreover, the NO2-sensing properties of the p-SnO/n-ZnO device were investigated under various relative humidity. Finally, the NO2-sensing mechanism of the p-SnO/n-ZnO nanowires was proposed and discussed.

DC Magnetron Sputtered IZTO Thin Films for Organic Photovoltaic Application.

IZTO20 (In0.6Zn0.2Sn0.2O1.5) ceramic target was prepared from oxide mixture of In2O3, ZnO, and SnO2 powders. IZTO20 thin films were then deposited onto glass substrate at 400 °C by DC magnetron sputtering. The average optical transmittance determined by ultraviolet-visible spectroscopy was higher than 85% for all films. The minimum resistivity of the annealed IZTO20 thin film was approximately 6.1×10-4 Ω·cm, which tended to increase with decreasing indium content. Substrate heating and annealing were found to be important parameters affecting the electrical and optical properties. An organic photovoltaic (OPV) cell was fabricated using the IZTO20 film deposited under the optimized condition as an anode electrode and the efficiency of up to 80% compared to that of a similar OPV cell using ITO film was observed. Reduction of surface roughness and electrical resistivity through annealing treatment was found to contribute to the improved efficiency of the OPV cell.

The Current Status of Quality of Reporting in Acupuncture Treatment Case Reports: An Analysis of the Core Journal in Korea.

OBJECTIVES: The present study aimed to evaluate the overall quality of case reports concerning acupuncture treatment in Korea. METHODS: We selected a representative Korean journal and retrieved eligible case reports on acupuncture treatment published from 2009 to 2015. We assessed the quality of reporting based on CAse REport (CARE) and STandards for Reporting Interventions in Clinical Trials of Acupuncture (STRICTA) guideline checklists. RESULTS: A total of 93 eligible case reports of acupuncture treatment were identified among the 107 articles screened. Overall quality of reporting in the case reports was generally acceptable (75.4% on CARE, 67.7% on STRICTA), but several crucial items remained substantially underreported. CONCLUSIONS: Endorsement of the CARE and STRICTA guidelines is needed to improve the completeness of reporting. Our findings will be helpful in developing a more appropriate reporting guideline for case reports in acupuncture treatment.

How do readers choose to undergo treatments based on medical articles?

The purpose of this study is to study the reader's cognitive process in reading medical articles and its influence on the decision-making process. Twenty-four participants completed a survey pertaining to 36 medical articles on new treatments with similar text structures and similar titles. Participants rated each article on its level of interest, informativeness, and reliability, and were asked whether they would choose the treatments in the news article. A cognitive decision-making model can be applied to health contexts, in which the reader's subjective ratings on interest, informativeness, and reliability were positively associated with choosing new treatments. The decision-making process path from the perception of informativeness was mediated by the reliability of the news article. Interest was positively linked to informativeness, although it was not directly associated with reliability. This study shows that readers' subjective ratings on health information can indicate their decision-making. Artifacts in the information that might incite emotions or interest, such as framing, can affect the reader's decision-making process.

Transmission electron microscopy study of 3.2 YSZ single crystals manufactured by the skull melting method.

Transmission electron microscopy (TEM) analyses were performed to examine the spontaneously ordered structure in single crystals of 3.2 mole% of Y2O3 added ZrO2 (3.2 YSZ) manufactured by the Skull melting method. The selected area electron diffraction patterns showed several super-structure reflections with symmetrical intensity at (100), (010), and (110) positions, indicating that Y0.5Zr0.5O(2-x) with L1(0)-like cation-ordered structure was formed in 3.2 YSZ. High-resolution TEM has been used to reveal the presence of the partially ordered structure, which was characterized by a doublet periodicity in the contrast of the {100} lattice planes.

Effects of temperature, target/substrate distance, and background pressure on growth of ZnO nanorods by pulsed laser deposition.

The growth of ZnO nanorods on the c-plane of Al2O3 substrates by PLD was been investigated by controlling processing conditions such as growth temperature, distance between target and substrate, and background oxygen pressure. ZnO nanorods were observed from the growth temperature of 600 degrees C for the oxygen pressure of 30 mTorr and the target/substrate distance of 70 mm. The diameters of the ZnO nanorods at the temperature of 700 degrees C and the oxygen pressure of 30 mTorr were approximately 200, 70, and 40 nm for the distance of 45, 70, and 100 mm, respectively. ZnO films without nanorods were observed at the distance of 70 mm and the temperature of 700 degrees C when the oxygen pressure decreased to 1 mTorr. The kinetic energy of the ablated particles by the laser decreases during collisions with background oxygen molecules, resulting in conditions that favor the growth of ZnO nanorods.

Anaerobic treatment of palm oil mill effluent using combined high-rate anaerobic reactors.

Combined system of high-rate anaerobic reactors for treating palm oil mill effluent (POME) was developed and investigated in this study. The system composed of one common primary hybrid reactor which was shared by two different secondary filter reactors. An overall COD removal efficiency of 93.5% was achieved in both systems. The secondary reactors contributed not only in enhancing the COD removal efficiency, but also ensured the performance stability of the entire system. Biomass remained intact in the secondary reactor in contrast to the primary reactor in which occasional washout of biomass was observed. The pH of POME was adjusted at the beginning of the operation, as the process continued POME did not require the external pH adjustment as the pH was maintained in desired range. The biogas was produced up to 110 l/d with the yield of 0.171-0.269 l [CH4]/g [COD removed] and 59.5-78.2% content of methane.

Low temperature growth and optical properties of ZnO nanowires using an aqueous solution method.

ZnO nanowires were grown on indium tin oxide (ITO) coated glass substrates at a low temperature of 90 degrees C using an aqueous solution method. The ZnO seeds were coated on the ITO thin films by using a spin coater. ZnO nanowires were formed in an aqueous solution containing zinc nitrate hexahydrate (Zn(NO3)2 x 6H2O) and hexamethylenetetramine (C6H12N4). The pH value and concentration of the solution play an important role in the growth and morphologies of ZnO nanowires. The size of ZnO naonowires increased as the concentration of the solution increased. It was formed with a top surface of hexagonal and tapered shape at low and high pH values respectively. Additionally, the single crystalline structure and optical property of the ZnO nanowires were investigated using high-resolution transmission electron microscopy and photoluminescence spectroscopy.

Dielectric properties of Ni-coated BaTiO/sub 3-/PMMA composite.

Dielectric properties of Ni-coated BaTiO(3)-PMMA (polymethyl methacrylate) composite were studied from an embedded capacitor application viewpoint. Volume loading of up to 50% was attempted, and the results were compared with uncoated BaTiO(3)-PMMA composite. Ni-coating on BaTiO(3) powder was found to greatly improve the dielectric properties of the composite, especially the dielectric constant value. K values of about 100 with temperature-stable X7E characteristics were realized.