RESUMO
Background: Patellar resurfacing is routinely performed during total knee arthroplasty to reduce pain associated with patellofemoral osteoarthritis. With 3-dimensional ingrowth materials readily available, the present study aimed to evaluate if cemented polyethylene (CP) patellar buttons conferred higher ultimate load to failure than press-fit metal-backed (PF) buttons in axial compression. Material and methods: Ten matched cadaveric and 20 composite patellae were resurfaced and implanted with either a PF or CP button. Biomechanical testing using an MTS machine was performed to measure the force required to generate a periprosthetic patella fracture. Mean load to failure and load to failure per 1-mm patellar thickness were compared with a paired and independent samples Students' t-test for the cadaveric and composite patellae, respectively. Results: The average load to failure for the matched cadaveric patellae with PF implants was significantly lower than that for patellae with CP buttons (4082.05 N vs 5898.37 N, P = .045). The average load to failure for composite patella with PF implants was significantly higher than that for composite patellae with CP implants (6004.09 N vs 4551.40 N, P = .001). The mean load to failure per 1-mm patellar thickness was also significantly higher for composite patellae with PF implants (263.80 N/mm vs 200.37 N/mm, P = .001). Conclusion: Cadaveric patellae with cemented implants had a significantly higher ultimate load to failure in axial compression than press-fit patella. However, this result was reversed in the composite model. Exploration of biological and composite model properties could provide further insight into patellar implant selection during total knee arthroplasty.