Preparation of hybrid film of polyaniline and organically pillared zirconium phosphate nanosheet by electrodeposition.

α-Zirconium phosphate was chemically modified with 1,2-bis(dimethylchlorosilyl)ethane to graft organic chain, and then it was used as host material for inorganic nanosheet-polyaniline hybrid. The grafted α-zirconium phosphate was exfoliated in an acetonitrile solution with tetrabutylammonium salt and aniline. The electrodeposition in the presence of aniline was performed, and then it resulted in a formation of higher-order structure in which phosphate nanosheet was propped up by 1,2-bis(dimethylchlorosilyl)ethane with intrusion of polyaniline into the nanospace. The gravimetric capacitance of the α-zirconium phosphate without grafts and polyaniline hybrid film was around 194 F/g with the base on the amount of polyaniline mass. On the other hand, the α-zirconium phosphate nanosheet with grafts and polyaniline hybrid film provided larger capacitance of around 350 F/g in maximum. The nanospace formed by grafted phosphate nanosheet with 1,2-bis(dimethylchlorosilyl)ethane molecules gives increased amounts of polyaniline included and diffusion paths for ions.

Synthesis, crystal structure, and magnetic properties of Bi3Mn4O12(NO3) oxynitrate comprising S = 3/2 honeycomb lattice.

Neutron diffraction and FT-IR analysis revealed that the novel oxynitrate Bi(3)Mn(4)O(12)(NO(3)) (space group P3, a = 4.9692(1) A, c = 13.1627(3) A) prepared by hydrothermal synthesis is of a new structural type including flat NO(3) layers alternating with blocks of two PbSb(2)O(6)-like layers. Mn(4+) (S = (3)/(2)) forms a regular honeycomb lattice, and magnetic susceptibility data indicated two-dimensional magnetism. Despite its Weiss constant of -257 K, no long-range ordering was observed down to 0.4 K because of the magnetic frustration due to the competition between the nearest and the next-nearest antiferromagnetic interactions.

Preparation of oriented titanium phosphate and tin phosphate/polyaniline hybrid films by electrochemical deposition.

The preparation of hybrid films of metal (Ti and Sn) phosphate nanosheets and polyaniline by simultaneous electrophoretic and electrolytic deposition was performed in an acetonitrile solvent. Emeraldine polyaniline was intercalated between the phosphate nanosheets with a monolayer arrangement. The obtained hybrid films were several tens of micrometers in thickness. The ratio of incorporated polyaniline to metal phosphate in the hybrid films reaches to around 0.45 and 0.30 at suitable concentrations of tetrabutylammonium hydroxide (TBAOH). These amounts correspond with occupancy of polyaniline in the interlayer gallery of several tens percent. Fractions of voids in a horizontal direction were around 22 and 1% in titanium phosphate/polyaniline and tin phosphate/polyaniline hybrid films, respectively. Thus, anodic electrodeposition makes it possible to form thick films of intercalation compounds of alpha-titanium and tin phosphates with polyaniline. These hybrid films were examined for redox activity. The cyclic voltammetry results of these films confirmed that the hybrid films have redox activity by polyaniline. For these voltammograms, the maximum current was observed in the tin phosphate/polyaniline hybrid deposited for 15 min. The redox activity of these hybrids possibly depends on the mesoscopic texture of the film, especially on the amount of voids in a horizontal direction.

Anodic electrodeposition of highly oriented zirconium phosphate and polyaniline-intercalated zirconium phosphate films.

Films of highly oriented alpha-zirconium phosphate and polyaniline-intercalated zirconium phosphate with controllable thickness in the micrometer range were grown anodically on Pt electrodes. To optimize the electrodeposition conditions, the exfoliation of alpha-zirconium phosphate by tetrabutylammonium (TBA) salts was investigated in several nonaqueous solvents. Acetonitrile was found to be the best solvent for making crack-free, oriented films because of its high vapor pressure, low viscosity, and relatively high permittivity. With TBA salts of neutral or weakly acidic anions (TBACl, TBABr, TBAI, TBA(HSO4), or TBA(H2PO4)), full exfoliation did not occur and alpha-zirconium phosphate and/or polyaniline were deposited as rough films. With basic anions (TBAF or TBAOH), dense, adherent films were obtained. X-ray diffraction patterns of the films showed that they were highly oriented along the stacking axis. The thickness could be controlled, up to about 40 microm, by limiting the time of the electrodeposition reaction. At monomer concentrations below 1.0 x 10(-2) mol/dm3, the emeraldine form of the intercalated polymer was obtained. Electrodeposition thus provides a thick film alternative to layer-by-layer assembly for intercalation compounds of alpha-zirconium phosphate with a conducting polymer.