RESUMO
The use of electronic devices that incorporate multilayer ceramic capacitors (MLCCs) is on the rise, requiring materials with good electrical properties and a narrow band gap. This study synthesized yttrium-substituted barium titanate (Ba1-x Y x TiO3, BYT) using a sol-gel process at 950 °C with varying concentrations of yttrium (0 ≤ x ≤ 0.3). X-ray diffraction analysis showed that the tetragonal phase became less pronounced as the yttrium content increased. The samples had varying grain sizes and porosity, with the BY30%T sample having the narrowest band gap at 2.21 eV. The BYT ceramic with 30% yttrium had a thermal conductivity of up to 7 W/m K and an electrical conductivity down to 0.002 (Ω cm)-1 at 180 °C. The current-voltage characteristics of the BYT MLCC were also studied, showing potential use in next-generation high-capacity MLCCs. This work presents BYT as a promising material for these types of capacitors.
RESUMO
The BTO, BFTC, and BCTF compounds were synthesized by the sol-gel method. The XRD study revealed the formation of single-phase tetragonal perovskite structures with the space group (P4mm). The crystalline parameters were studied as a function of Fe and Co contents and occupation of Ba and/or Ti sites by Fe and Co in the BTO lattice. It was found that the obtained strain increases when Ba2+ is substituted by Co2+ and Ti4+ by Fe3+. The Raman investigation confirmed the existence of three active modes (B1/E (TO1LO), (E (TO)/A1(TO3), and (A 1(LO)/E (TO), all of which are related to the existence of the tetragonal phase and strongly support the XRD results. The microstructural study showed a clear correlation between the presence of Fe and Co and the grain size distribution. Optical studies revealed the improvement in band gap energy with transition-metal (Fe and Co) co-doped BTO ceramics. The decrease in the band gap is explained by the competing effects of Columbian interactions, microdeformation, and oxygen defects. The results indicate that the presence of Fe and Co dopants enhances the absorption in the BTO ceramic. The dopants demonstrated an effect on thermal conductivity: they decreased the thermal conductivity of BTO, which is in the range of 0.76-2.23 W m-1 K-1 at room temperature and 2.02-0.27 W m-1 K-1 at elevated temperatures. The microstructure of the manufactured materials and the grain size distribution affect the compressive strength.
RESUMO
The catalytic hydrogenation of 2,4-dinitrotoluene (DNT) to 2,4-toluenediamine (TDA) is a key step in the production of polyurethanes; therefore, the development of efficient hydrogenation catalysts for industrial use is of paramount importance. In the present study, chromium(IV) oxide nanowires were decorated by palladium and platinum nanoparticles in a one-step, simple, and fast preparation method to yield highly efficient hydrogenation catalysts for immediate use. The nanoparticles were deposited onto the surface of CrO2 nanowires by using ultrasonic cavitation and ethanol as a reduction agent. Beneficially, the catalyst became catalytically active right at the end of the preparation and no further treatment was necessary. The activity of the Pd- and Pt-decorated CrO2 catalysts were compared in the hydrogenation of 2,4-dinitrotoluene (DNT). Both catalysts have shown high activity in the hydrogenation tests. The DNT conversion exceeded 98% in both cases, whereas the 2,4-toluenediamine (TDA) yields were 99.7 n/n% and 98.8 n/n%, with the Pd/CrO2 and Pt/CrO2, respectively, at 333 K and 20 bar H2 pressure. In the case of the Pt/CrO2 catalyst, 304.08 mol of TDA formed with 1 mol Pt after 1 h hydrogenation. Activation energies were also calculated to be approximately 24 kJâmol-1. Besides their immediate applicability, our catalysts were well dispersible in the reaction medium (methanolic solution of DNT). Moreover, because of their magnetic behavior, the catalysts were easy to handle and remove from the reaction media by using a magnetic field.