A Facile One-Pot Synthesis of Hierarchically Organized Carbon/TiO2 Monoliths with Ordered Mesopores.

Sol-gel processing combined with soft templating and gelation-induced phase separation is very sensitive to the precursor sol composition. In this work we present a straightforward synthesis towards hierarchically structured, macroporous carbon/titania monoliths with ordered mesopores derived from resorcinol/formaldehyde monoliths and a glycolated titanium precursor. We demonstrate the influence of various reaction solvents, where diol-based media and the proportion of the catalyst seem to be essential in controlling spinodal decomposition, obtaining similar monolithic structures under different synthesis conditions. Based on these observations, we further homogeneously incorporated TiO2 into the carbon structure by an in situ synthesis approach, obtaining structural features similar to pure carbon materials with surface areas of about 400 m2 g-1 , periodically arranged mesopores with a mean distance of 10-11 nm and cellular macroporosity.

Towards Real-Time Ion-Specific Structural Sensitivity in Nanoporous Carbon Electrodes Using In Situ Anomalous Small-Angle X-ray Scattering.

Current in situ techniques to study ion charge storage and electrical double-layer formation in nanoporous electrodes are either chemically sensitive to element-specific concentration changes or structurally sensitive to rearrangements of ions and solvent molecules; but rarely can they cover both. Here we introduce in situ anomalous small-angle X-ray scattering (ASAXS) as a unique method to extract both real-time structural and ion-specific chemical information from one single experiment. Using a 1 M RbBr aqueous electrolyte and a hierarchical micro- and mesoporous carbon electrode, we identify different charging mechanisms for positive and negative applied potentials. We are able not only to track the global concentration change of each ion species individually, but also to observe their individual local rearrangement within the pore space.

In Situ Measurement of Electrosorption-Induced Deformation Reveals the Importance of Micropores in Hierarchical Carbons.

Dimensional changes in carbon-based supercapacitor electrodes were investigated using a combination of electrochemical dilatometry and in situ small-angle X-ray scattering. A novel hierarchical carbon material with ordered mesoporosity was synthesized, providing the unique possibility to track electrode expansion and shrinkage on the nanometer scale and the macroscopic scale simultaneously. Two carbons with similar mesopore structure but different amounts of micropores were investigated, employing two different aqueous electrolytes. The strain of the electrodes was always positive, but asymmetric with respect to positive and negative applied voltages. The asymmetry strongly increased with increasing microporosity, giving hints to the possible physical origin of electrosorption induced pore swelling.