RESUMO
This work consisted in the preparation of platinum-based catalysts supported on carbon (Vulcan XC-72) and investigation of their physicochemical and electrochemical properties. Catalysts of the C/Pt-Ni-Sn-Me (Me = Ru or Ir) type were prepared by the Pechini method at temperature of 350°C. Four different compositions were homemade: C/Pt(60)Sn(10)Ni(30), C/Pt(60)Sn(10)Ni(20)Ru(10), C/Pt(60)Sn(10)Ni(10)Ru(20), and C/Pt(60)Sn(10)Ni(10)Ir(20). These catalysts were electrochemically and physically characterized by cyclic voltammetry (CV), chronoamperometry (CA) in the presence of glycerol 1.0 mol dm(-3), X-ray diffraction (XRD), and high-resolution transmission electron microscopy (HRTEM). XRD results showed the main peaks of face-centered cubic Pt. The particle sizes obtained from XRD and HRTEM experiments were close to values ranging from 3 to 8.5 nm. The CV results indicate behavior typical of Pt-based catalysts in acid medium. The CV and CA data reveal that quaternary catalysts present the highest current density for the electrooxidation of glycerol.
Assuntos
Eletroquímica/métodos , Glicerol/química , Carbono/química , Catálise , Microscopia Eletrônica de Transmissão , Nanotecnologia/métodos , Oxirredução , Tamanho da Partícula , Platina/química , Difração de Raios XRESUMO
Carbon supported Pt-Au catalysts with different bimetallic compositions were prepared by water in oil (w/o) microemulsion. Carbon Vulcan XC-72 was added during the synthesis of particles in order to obtain their good dispersion and a mean particle size distribution of 5.02 +/- 0.56 nm. Structural characterization was performed using XRD at wide angles (WAXS), which showed that Pt-Au particles exhibited alloy properties. Electrochemical characterization allowed to estimate the surface composition of Pt-Au alloys, which was close to that of the bulk material Pt(20)Au(80). This catalyst composition displayed the best catalytic activity in steady-state conditions in comparison with Pt(50)Au(50) or Pt and Au alone. Moreover, a Pt-Au/C catalyst with a metal loading of 40 wt % was immobilized onto a carbon porous tube as anode. A membrane-less biofuel cell was tested using laccase/ABTS biocathode in phosphate buffer (pH 5).