Bio-based composites were developed from the epoxy derivatives of Lallemantia iberica oil and kraft lignin (ELALO and EpLnK), using UV radiation as a low energy consumption tool for the oxiranes reaction. To avoid the filler sedimentation or its inhomogeneous distribution in the oil matrix, different structure-directing agents (SDA) were employed: 1,3:2,4-dibenzylidene-D-sorbitol (DBS), 12-hydroxystearic acid (HSA) and sorbitan monostearate (Span 60). The SDA and EpLnK effect upon the ELALO-based formulations, their curing reaction and the performance of the resulting materials were investigated. Fourier-transform Infrared Spectrometry (FTIR) indicates different modes of molecular arrangement through H bonds for the initial ELALO-SDA or ELALO-SDA-EpLnK systems, also confirming the epoxy group's reaction through the cationic mechanism for the final composites. Gel fraction measurements validate the significant conversion of the epoxides for those materials containing SDAs or 1% EpLnK; an increased EpLnK amount (5%), with or without SDA addition, conduced to an inefficient polymerization process, with the UV radiation being partially absorbed by the filler. Thermo-gravimetric and dynamic-mechanical analyses (TGA and DMA) revealed good properties for the ELALO-based materials. By loading 1% EpLnK, the thermal stability was improved to with 10 °C (for Td3%) and the addition of each SDA differently influenced the Tg values but also gave differences in the glassy and rubbery states when the storage moduli were interrogated, depending on their chemical structures. Water affinity and morphological studies were also carried out.

Composite Materials from Renewable Resources as Sustainable Corrosion Protection Coatings.

Epoxidized linseed oil (ELO) and kraft lignin (LnK) were used to obtain new sustainable composites as corrosion protection layers through a double-curing procedure involving UV radiation and thermal curing to ensure homogeneous distribution of the filler. The crosslinked structures were confirmed by Fourier-transform infrared spectrometry (FTIR), by comparative monitorization of the absorption band at 825 cm-1, attributed to the stretching vibration of epoxy rings. Thermal degradation behavior under N2 gas indicates that the higher LnK content, the better thermal stability of the composites (over 30 °C of Td10% for ELO + 15% LnK), while for the experiment under air-oxidant atmosphere, the lower LnK content (5%) conducted to the more thermo-stable material. Dynamic-mechanic behavior and water affinity of the new materials were also investigated. The increase of the Tg values with the increase of the LnK content (20 °C for the composite with 15% LnK) denote the reinforcement effect of the LnK, while the surface and bulk water affinity were not dramatically affected. All the obtained composites were tested as carbon steel corrosion protection coatings, resulting in significant increase of corrosion inhibition efficiency (IE) of 140-380%, highlighting the great potential of the bio-based ELO-LnK composites as a future perspective for industrial application.