RESUMO
To develop novel biodegradable biomedical materials, polylactide-grafted dextrans (Dex-g-PLA)s having various lengths, numbers of graft chains and sugar units were synthesized using the trimethylsilyl (TMS) protection method. To explore the possibility of using Dex-g-PLA as a biomedical soft-material, the contact angle, cell attachment and protein adsorption properties of the films prepared from these biodegradable and amphiphilic graft co-polymers were investigated. The poly-L-lactide (PLLA) film did not absorb water at all because of its high hydrophobicity, while the graft co-polymer films started immediately to swell after immersion in PBS. The percentage of water absorption at equilibrium increased with increasing sugar unit content. The receding contact angle of the Dex-g-PLA films against water was smaller than that of the PLLA film. The receding contact angle of Dex-g-PLA films against water decreased with increasing the sugar unit content. The top surface of the Dex-g-PLA film was suggested to be covered with hydrophilic Dex segments by means of annealing in water and to afford the wettable surface. Such a wettable surface led to the suppression of cell attachment and protein adsorption onto the film.
Assuntos
Dextranos/química , Poliésteres/química , Albumina Sérica/química , Adsorção , Animais , Bovinos , Adesão Celular , Linhagem Celular , Camundongos , Microscopia Eletrônica de Varredura , Estrutura Molecular , Temperatura , Água/químicaRESUMO
Polylactide (PLA)-grafted dextran (Dex-graft-PLA) of various contents of sugar units was synthesized by anionic polymerization of L-lactide (L-LA) using the alkoxide of partially trimethylsilylated dextran (TMSDex) and subsequently removing the trimethylsilyl (TMS) groups. The copolymer showed different solubility from L-LA homopolymer with increasing the content of sugar units. We prepared bovine serum albumin (BSA)-loaded microspheres (MS)s according to a water-in-oil-in-water emulsion-solvent evaporation/extraction method using methylene chloride/DMSO as an organic cosolvent. MSs prepared from Dex-graft-PLA [MS(Dex-graft-PLA)s] exhibited higher loading efficiency of BSA than MSs prepared from PLLA [MS(PLLA)s]. The in vitro release rate of BSA from MS(Dex-graft-PLA) was faster than that from MS(PLLA). BSA released from MS(Dex-graft-PLA) maintained the secondary structure of native BSA to a great extent, compared with BSA released from MS(PLLA).