RESUMO
As cementation represents the last stage of the work involved in making various indirect restorations (metal ceramic crowns and bridges, full ceramic crowns and bridges, inlays, onlays, and fiber posts), its quality significantly contributes to the clinical success of the therapy performed. In the last two decades, the demand for ceramic indirect restorations in everyday dental practice has considerably increased primarily due to the growing significance of esthetics among patients, but also as a result of hypersensitivity reactions to dental alloys in some individuals. In this context, it is essential to ensure a permanent and reliable adhesive bond between the indirect restoration and the tooth structure, as this is the key to the success of aesthetic restorations. Resin-based luting materials benefit from excellent optical (aesthetic) and mechanical properties, as well as from providing a strong and durable adhesive bond between the restoration and the tooth. For this reason, resin cements are a reliable choice of material for cementing polycrystalline ceramic restorations. The current dental material market offers a wide range of resin cement with diverse and continually advancing properties. In response, we wish to note that the interest in the properties of resin-based cements among clinicians has existed for many years. Yet, despite extensive research on the subject and the resulting continued improvements in the quality of these materials, there is still no ideal resin-based cement on the market. The manuscript authors were guided by this fact when writing the article content, as the aim was to provide a concise overview of the composition, properties, and current trends, as well as some future guidelines for research in this field that would be beneficial for dental practitioners as well as the scientific community. It is extremely important to provide reliable and succinct information and guidelines for resin luting materials for dental dental practitioners.
RESUMO
As the mechanical properties of resin-based dental composite materials are highly relevant in clinical practice, diverse strategies for their potential enhancement have been proposed in the extant literature, aiming to facilitate their reliable use in dental medicine. In this context, the focus is primarily given to the mechanical properties with the greatest influence on clinical success, i.e., the longevity of the filling in the patient's mouth and its ability to withstand very strong masticatory forces. Guided by these objectives, the goal of the present study was to ascertain whether the reinforcement of dental composite resins with electrospun polyamide (PA) nanofibers would improve the mechanical strength of dental restoration materials. For this purpose, light-cure dental composite resins were interspersed with one and two layers comprising PA nanofibers in order to investigate the influence of such reinforcement on the mechanical properties of the resulting hybrid resins. One set of the obtained samples was investigated as prepared, while another set was immersed in artificial saliva for 14 days and was subsequently subjected to the same set of analyses, namely Fourier-transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), and differential scanning calorimetry (DSC). Findings yielded by the FTIR analysis confirmed the structure of the produced dental composite resin material. They also provided evidence that, while the presence of PA nanofibers did not influence the curing process, it strengthened the dental composite resin. Moreover, flexural strength measurements revealed that the inclusion of a 16 µm-thick PA nanolayer enabled the dental composite resin to withstand a load of 3.2 MPa. These findings were supported by the SEM results, which further indicated that immersing the resin in saline solution resulted in a more compact composite material structure. Finally, DSC results indicated that as-prepared as well as saline-treated reinforced samples had a lower glass transition temperature (Tg) compared to pure resin. Specifically, while pure resin had a Tg of 61.6 °C, each additional PA nanolayer decreased the Tg by about 2 °C, while the further reduction was obtained when samples were immersed in saline for 14 days. These results show that electrospinning is a facile method for producing different nanofibers that can be incorporated into resin-based dental composite materials to modify their mechanical properties. Moreover, while their inclusion strengthens the resin-based dental composite materials, it does not affect the course and outcome of the polymerization reaction, which is an important factor for their use in clinical practice.
