Features of Phase Formation of Pyrochlore-type Ceramics Bi2Mg(Zn)1-x Ni x Ta2O9.

The phase formation of complex pyrochlores (space group Fd-3m) Bi2Mg(Zn)1-x Ni x Ta2O9 was investigated during solid-phase synthesis. It was found that the pyrochlore phase precursor in all cases was α-BiTaO4. The pyrochlore phase synthesis reaction proceeds mainly at temperatures above 850-900 °C and consists in the interaction of bismuth orthotantalate with a transition element oxide. The influence of magnesium and zinc on the course of pyrochlore synthesis was revealed. The reaction temperatures of magnesium and nickel (800 and 750 °C, respectively) were determined. The change in the pyrochlore unit cell parameter depending on the synthesis temperature was analyzed for both systems. Nickel-magnesium pyrochlores are characterized by a porous dendrite-like microstructure with a grain size of 0.5-1.0 microns, and the porosity of the samples reaches 20 percent. The calcination temperature does not significantly affect the microstructure of the samples. Prolonged calcination of the preparations leads to the coalescence of grains with the formation of larger particles. Nickel oxide has a sintering effect on ceramics. The studied nickel-zinc pyrochlores are characterized by a low-porous dense microstructure. The porosity of the samples does not exceed 10%. The optimal conditions for obtaining phase-pure pyrochlores (1050 °C and 15 h) were determined.

The Identification of Cu-O-C Bond in Cu/MWCNTs Hybrid Nanocomposite by XPS and NEXAFS Spectroscopy.

The results of the research of a composite based on multi-walled carbon nanotubes (MWCNTs) decorated with CuO/Cu2O/Cu nanoparticles deposited by the cupric formate pyrolysis are discussed. The study used a complementary set of methods, including scanning and transmission electron microscopy, X-ray diffractometry, Raman, and ultrasoft X-ray spectroscopy. The investigation results show the good adhesion between the copper nanoparticles coating and the MWCNT surface through the oxygen atom bridge formation between the carbon atoms of the MWCNT outer graphene layer and the oxygen atoms of CuO and Cu2O oxides. The formation of the Cu-O-C bond between the coating layer and the outer nanotube surface is clearly confirmed by the results of the O 1s near edge X-ray absorption fine structure (NEXAFS) and X-ray photoelectron spectroscopy (XPS) of the Cu/MWCNTs nanocomposite. The XPS measurements were performed using a laboratory spectrometer with sample charge compensation, and the NEXAFS studies were carried out using the synchrotron radiation of the Russian-German dipole beamline at BESSY-II (Berlin, Germany) and the NanoPES station at the Kurchatov Center for Synchrotron Radiation and Nanotechnology (Moscow, Russia).