RESUMO
Bioactive materials may be applied in tissue regeneration, and an example of such materials are wound dressings, which are used to accelerate skin healing, especially after trauma. Here, we proposed a novel dressing enriched by a bioactive component. The aim of our study was to prepare and characterize poly(vinyl alcohol) films modified with strontium titanate nanoparticles. The physicochemical properties of films were studied, such as surface free energy and surface roughness, as well as the mechanical properties of materials. Moreover, different biological studies were carried out, like in vitro hemo- and cyto-compatibility, biocidal activity, and anti-biofilm formation. Also, the degradation of the materials' utilization possibilities and enzymatic activity in compost were checked. The decrease of surface free energy, increase of roughness, and improvement of mechanical strength were found after the addition of nanoparticles. All developed films were cyto-compatible, and did not induce a hemolytic effect on the human erythrocytes. The PVA films containing the highest concentration of STO (20%) reduced the proliferation of Eschericha coli, Pseudomonas aeruginosa, and Staphylococcus aureus significantly. Also, all films were characterized by surface anti-biofilm activity, as they significantly lowered the bacterial biofilm abundance and its dehydrogenase activity. The films were degraded by the compost microorganism. However, PVA with the addition of 20%STO was more difficult to degrade. Based on our results, for wound dressing application, we suggest using bioactive films based on PVA + 20%STO, as they were characterized by high antibacterial properties, favorable physicochemical characteristics, and good biocompatibility with human cells.
RESUMO
This study focuses on the fabrication of polymer nanocomposite films using polyvinyl alcohol (PVA)/graphene quantum dots (GQDs). We investigate the relationship between the structural, thermal, and nanoscale morphological properties of these films and their photoluminescent response. Although according to X-ray diffraction (XRD), Fourier-transform infrared spectroscopy (FT-IR), and differential thermal analysis (DTA), the incorporation of GQDs does not significantly affect the percentage crystallinity of the PVA matrix, for a range of added GQD concentrations, atomic force microscopy (AFM) showed the formation of islands with apparent crystalline morphology on the surface of the PVA/GQD films. This observation suggests that GQDs presumably act as nucleating agents for island growth. The incorporation of GQDs also led to the formation of characteristic surface pores with increased stiffness and frictional contrast, as indicated by ultrasonic force microscopy (UFM) and frictional force microscopy (FFM) data. The photoluminescence (PL) spectra of the films were found to depend both on the amount of GQDs incorporated and on the film morphology. For GQD loads >1.2%wt, a GQD-related band was observed at ~1650 cm-1 in FT-IR, along with an increase in the PL band at lower energy. For a load of ~2%wt GQDs, the surface morphology was characterized by extended cluster aggregates with lower stiffness and friction than the surrounding matrix, and the PL signal decreased.