RESUMO
The aim of the paper is to design, manufacture, and test an off-axis composite profile of circular cross-section. Composite profile based on continuous carbon fibers reinforcing the onyx matrix, i.e., a matrix that consists of nylon and micro carbon fibers, was produced by fused deposition modeling (FDM) method. A buckling test of the six printed composite specimens was performed on a tensile test machine. The values of the experiment were compared with the values of the computational simulation using the Finite Element Method (FEM) analysis. The mean value of the experimentally determined critical force at which the composite profile failed was 3102 N, while the value of the critical force by FEM analysis was calculated to be 2879 N. Thus, reliability of the simulation to determine the critical force differed from the experimental procedure by only 7%. FEM analysis revealed that the primary failure of 3D printed composite parts was not due to loss of stability, but due to material failure. With great accuracy, the results of the comparison show that it is possible to predict the mechanical properties of 3D printed composite laminates on the basis of a theoretical model.
RESUMO
The aim of this work was to monitor the mechanical behavior of 316L stainless steel produced by 3D printing in the vertical direction. The material was tested in the "as printed" state. Digital Image Correlation measurements were used for 4 types of notched specimens. The behavior of these specimens under monotonic loading was investigated in two loading paths: tension and torsion. Based on the experimental data, two yield criteria were used in the finite element analyses. Von Mises criterion and Hill criterion were applied, together with the nonlinear isotropic hardening rule of Voce. Subsequently, the load-deformation responses of simulations and experiments were compared. Results of the Hill criterion show better correlation with experimental data. The numerical study shows that taking into account the difference in yield stress in the horizontal direction of printing plays a crucial role for modeling of notched geometries loaded in the vertical direction of printing. Ductility of 3D printed specimens in the "as printed" state is also compared with 3D printed machined specimens and specimens produced by conventional methods. "As printed" specimens have 2/3 lower ductility than specimens produced by a conventional production method. Machining of "as printed" specimens does not affect the yield stress, but a significant reduction of ductility was observed due to microcracks arising from the pores as a microscopic surface study showed.