Effect of Loading and Heating History on Deformation of LaCoO3.

The aim of this work was to study cyclic stress-strain deformation behavior of LaCoO3 as a function of loading and heating history. The ferroelastic hysteretic deformation of LaCoO3 at different stresses and temperatures was characterized using effective Young's modulus, hysteresis loop area and creep strain shift parameters. The deformation behavior of LaCoO3 was not significantly affected by the previous loading and heating history when tested at constant temperature. The high temperature strength and Young's modulus of LaCoO3 were higher compared to at room temperature. A creep strain shift parameter was introduced to characterize creep strain in LaCoO3 for the first time.

Spark Plasma Sintered B4C-Structural, Thermal, Electrical and Mechanical Properties.

The structural, thermal, electrical and mechanical properties of fully dense B4C ceramics, sintered using Spark Plasma Sintering (SPS), were studied and compared to the properties of B4C ceramics previously published in the literature. New results on B4C's mechanical responses were obtained by nanoindentation and ring-on-ring biaxial strength testing. The findings contribute to a more complete knowledge of the properties of B4C ceramics, an important material in many industrial applications.

Silicon Oxycarbide-Tin Nanocomposite as a High-Power-Density Anode for Li-Ion Batteries.

Tin-based materials are an emerging class of Li-ion anodes with considerable potential for use in high-energy-density Li-ion batteries. However, the long-lasting electrochemical performance of Sn remains a formidable challenge due to the large volume changes occurring upon its lithiation. The prevailing approaches toward stabilization of such electrodes involve embedding Sn in the form of nanoparticles (NPs) in an active/inactive matrix. The matrix helps to buffer the volume changes of Sn, impart better electronic connectivity and prevent particle aggregation upon lithiation/delithiation. Herein, facile synthesis of Sn NPs embedded in a SiOC matrix via the pyrolysis of a preceramic polymer as a single-source precursor is reported. This polymer contains Sn 2-ethyl-hexanoate (Sn(Oct)2) and poly(methylhydrosiloxane) as sources of Sn and Si, respectively. Upon functionalization with apolar divinyl benzene sidechains, the polymer is rendered compatible with Sn(Oct)2. This approach yields a homogeneous dispersion of Sn NPs in a SiOC matrix with sizes on the order of 5-30 nm. Anodes of the SiOC/Sn nanocomposite demonstrate high capacities of 644 and 553 mAh g-1 at current densities of 74.4 and 2232 mA g-1 (C/5 and 6C rates for graphite), respectively, and show superior rate capability with only 14% capacity decay at high currents.

Pulsed UV Laser Processing of Carbosilane and Silazane Polymers.

Freestanding SiCNO ceramic pieces with sub-mm features were produced by laser crosslinking of carbosilane and silazane polymer precursors followed by pyrolysis in inert atmosphere. Three different pulsed UV laser systems were investigated, and the influence of laser wavelength, operating power and scanning speed were all found to be important. Different photoinitiators were tested for the two lasers operating at 355 nm, while for the 266 nm laser, crosslinking occurred also without photoinitiator. Pre-treatment of glass substrates with fluorinated silanes was found to ease the release of green bodies during solvent development. Polymer crosslinking was observed with all three of the laser systems, as were bubbles, surface charring and in some cases ablation. By focusing the laser beam several millimeters above the surface of the resin, selective polymer crosslinking was observed exclusively.

Torsional shear strength of steel joined with high performance aerospace adhesives at cryogenic and elevated temperatures.

Pure torsional shear tests of joints glued with two different aerospace grade adhesives were performed using a specifically designed and constructed torsional shear test equipment. The developed test equipment allows for measuring of pure torsional shear strength under cryogenic and at elevated temperature conditions. The adhesives Hysol EA 9321 and 3M Scotch-Weld EC-9323-2 B/A were used to join steel torsional shear test specimens. Torsional shear tests were performed from -180°C to 150°C. In addition torsional shear fatigue tests were also performed at various loads and the effect of cryogenic aging (cyclic cooling and warming) on the torsional strength of the joints was investigated. The results showed that both sets of adhesive joints achieved three times higher torsional shear strength at -180°C compared to room temperature.

Rapid carbon nanotubes suspension in organic solvents using organosilicon polymers.

A strategy for a simple dispersion of commercial multi-walled carbon nanotubes (MWCNTs) using two organosilicones, polycarbosilane SMP10 and polysilazane Ceraset PSZ20, in organic solvents such as cyclohexane, tetrahydrofuran (THF), m-xylene and chloroform is presented. In just a few minutes the combined action of sonication and the presence of Pt(0) catalyst is sufficient to obtain a homogeneous suspension, thanks to the rapid hydrosilylation reaction between SiH groups of the polymer and the CNT sidewall. The as-produced suspensions have a particle size distribution <1µm and remain unchanged after several months. A maximum of 0.47 and 0.50mg/ml was achieved, respectively, for Ceraset in THF and SMP10 in chloroform. Possible applications as polymeric and ceramic thin films or aerogels are presented.

Ceramic Spheres-A Novel Solution to Deep Sea Buoyancy Modules.

Ceramic-based hollow spheres are considered a great driving force for many applications such as offshore buoyancy modules due to their large diameter to wall thickness ratio and uniform wall thickness geometric features. We have developed such thin-walled hollow spheres made of alumina using slip casting and sintering processes. A diameter as large as 50 mm with a wall thickness of 0.5-1.0 mm has been successfully achieved in these spheres. Their material and structural properties were examined by a series of characterization tools. Particularly, the feasibility of these spheres was investigated with respect to its application for deep sea (>3000 m) buoyancy modules. These spheres, sintered at 1600 °C and with 1.0 mm of wall thickness, have achieved buoyancy of more than 54%. As the sphere's wall thickness was reduced (e.g., 0.5 mm), their buoyancy reached 72%. The mechanical performance of such spheres has shown a hydrostatic failure pressure above 150 MPa, corresponding to a rating depth below sea level of 5000 m considering a safety factor of 3. The developed alumina-based ceramic spheres are feasible for low cost and scaled-up production and show great potential at depths greater than those achievable by the current deep-sea buoyancy module technologies.

Cytotoxicity evaluation of polymer-derived ceramics for pacemaker electrode applications.

Ceramics are known to be chemically stable, and the possibility to electrically dope polymer-derived ceramics makes it a material of interest for implantable electrode applications. We investigated cytotoxic characteristics of four polymer-derived ceramic candidates with either electrically conductive or insulating properties. Cytotoxicity was assessed by culturing C2C12 myoblast cells under two conditions: by exposing them to material extracts and by putting them directly in contact with material samples. Cell spreading was optically evaluated by comparing microscope observations immediately after the materials insertion and after 24 h culturing. Cell viability (MTT) and mortality (LDH) were quantified after 24-h incubation in contact with the materials. Comparison was made with biocompatible positive references (alumina, platinum, biocompatible stainless steel 1.4435), negative references (latex, stainless steel 1.4301) and controls (no material present in the culture wells). We found that the cytotoxic properties of tested ceramics are comparable to established reference materials. These ceramics, which are reported to be very stable, can be microstructured and electrically doped to a wide range of conductivity and are thus excellent candidates for implantable electrode applications including pacemakers.

Are asymmetric metal markings on the cone surface of ceramic femoral heads an indication of entrapped debris?

BACKGROUND: The probability of in vivo failure of ceramic hip joint implants is very low (0.004-0.05%). In addition to material flaws and overloading, improper handling during implantation can induce fractures of the ceramic ball head in the long term. Identifying the causes of an in vivo fracture contributes to improved understanding and potentially to further reduction of the fracture probability for patients. Asymmetric metal markings on the cone surface of in vivo ball head fractures have been reported. The question, therefore, is whether asymmetric loading is the sole cause or whether additional factors, specifically contamination entrapped in the taper fit, also contribute or are even the main cause. METHODS: The influence of the asymmetric physiological load configuration on resulting metal markings in the cone surface of an alumina femoral ball head with and without biological contaminants was investigated. Static and cyclic tests on ball heads were carried out in a load configuration of 0° (axisymmetric) and 40° in a physiological environment. The analysis of the metal marking was carried out to gain a better understanding of the processes that contribute to the generation of metal marking. Fractography was carried out to determine the fracture initiation of failed ball heads. RESULTS: Different types and sizes of residuals entrapped in the conical surface are shown to yield strongly asymmetric metal marking patterns. All heads tested without contaminants exhibited an almost homogenous distribution of residual metal markings around the circumference of the ceramic cone surface at the proximal end of the bore hole. The failure of ball heads that contained entrapped contaminants revealed a common fracture pattern. The site of fracture initiation on two of the failed heads was in the entrance region of the bore hole on the superior half of the head. CONCLUSION: Asymmetric metal markings observed on the ball heads tested in this investigation are most probably caused by the presence of contaminants entrapped in the taper fit. Homogenous metal mark distributions around the circumference indicate proper assembly of the ball head without entrapped contaminants. It should, however, be noted that different taper designs may possibly result in different marking patterns.

In situ ESEM observation of melting silver and Inconel on an Al(2)O(3) powder bed.

A hot stage in an environmental scanning electron microscope (ESEM) was used for in situ infiltration experiments. Pressureless infiltration of a porous Ti-activated Al(2)O(3) preform has been investigated at temperatures up to 1530 degrees C under two atmospheres (He and H(2)O((g))). A brief description of the operating and the experimental set-up is given. Silver and Inconel (Ni superalloy) infiltration experiments demonstrate the in situ potential of the ESEM at temperatures up to 1500 degrees C.