Development of dental inspection method: Nondestructive evaluation of an adhesive interface by ACTIVE acoustic emission.

PURPOSE: This study aims to confirm the usefulness of active acoustic emission (Active AE) for reproducible and non-invasive generation of physical external force which is required for conventional AE. METHODS: Experiment 1: A root dentin-resin adhesive interface was observed. The post space was filled with a dual-cure resin composite core material with and without adhesive. The vibration characteristics of the data obtained from the time-frequency analysis were evaluated. Experiment 2: A crown-abutment tooth adhesive interface was observed. Adhesive resin cement was used for luting the crown and adhesion states in the same specimen over time were analyzed with three measurements: at trial-fitting, immediately after luting, and 2 weeks after luting. Data were subjected to time-frequency analysis and relationships between amplitude (indicating loudness) and frequency (indicating the sound component) were analyzed. RESULTS: Experiment 1: Time-frequency analysis confirmed multiple peak frequencies for each specimen without adhesive and monomodal peak frequency in all specimens using adhesive. Experiment 2: Two weeks after luting, all specimens showed a single major peak except one which showed multiple weak peaks. The three-dimensional visualization of time-frequency analysis revealed one specimen with multiple weak peaks while all others displayed a single, low-amplitude band at 2 weeks after luting. CONCLUSION: The state of the adhesive interface can be evaluated using active AE. This basic technique may prove useful to evaluate changes in the adhesive interface of prostheses over time.

Development of dental inspection method: nondestructive evaluation of a dentin-adhesive interface by acoustic emission.

Purpose The state of adhesion between root dentin and a resin composite core material was inspected using acoustic emission (AE).Methods A total of 14 human incisors and premolars were used to prepare "no-adhesive group" and "adhesive group" specimens. For "adhesive group" specimens, a bonding agent was applied to root canal dentin. The entire post space was subsequently filled with a resin composite for both specimen groups. The prepared specimens were fixed onto a jig on which an AE sensor was installed. A zirconia ball was used for the impact test, and a vibration wave generated by the collision was measured by the system using an AE sensor. The obtained data were subjected to time-frequency analysis using analysis software (LabVIEW), and the relationship between the amplitude indicating the loudness and the frequency indicating the sound component was analyzed.Results Zirconia-ball collision tests using AE revealed differences between the groups with respect to the waveform of vibration waves transmitted to the root dentin through the root dentin-resin interface. The time-frequency analysis of the obtained data confirmed that multiple peaks were observed for each specimen in the no-adhesive group, whereas a single characteristic vibration peak was observed for all specimens in the adhesive group.Conclusions The state of the adhesive interface was successfully evaluated by AE. This demonstration is expected to lead to the development of a device that can detect problems at the bonding interface between the prostheses and tooth substances.