RESUMO
Superconductors are materials with zero electrical resistivity and the ability to expel magnetic fields, which is known as the Meissner effect. Their dissipationless diamagnetic response is central to magnetic levitation and circuits such as quantum interference devices. In this work, we used superconducting diamagnetism to shape the magnetic environment governing the transport of spin waves-collective spin excitations in magnets that are promising on-chip signal carriers-in a thin-film magnet. Using diamond-based magnetic imaging, we observed hybridized spin-wave-Meissner-current transport modes with strongly altered, temperature-tunable wavelengths and then demonstrated local control of spin-wave refraction using a focused laser. Our results demonstrate the versatility of superconductor-manipulated spin-wave transport and have potential applications in spin-wave gratings, filters, crystals, and cavities.
RESUMO
Exchange-bias has been reported in bulk nanocrystalline Fe2MnAl, but individual thin films of this Heusler alloy have never been studied so far. Here we study the structural and magnetic properties of nanocrystalline thin films of Fe2-x Mn1+x Al (x = -0.25, 0 and 0.25) obtained by sputtering and ex situ post-deposition annealing. We find that Fe2MnAl films display exchange-bias, and that varying Mn concentration determines the magnitude of the effect, which can be either enhanced (in Fe1.75Mn1.25Al) or suppressed (in Fe2.25Mn0.75Al). X-ray diffraction shows that our films present a mixed L21-B2 Heusler structure where increasing Mn concentration favors the partial transformation of the L21 phase into the B2 phase. Scanning transmission electron microscopy (STEM) and energy dispersive X-ray spectroscopy (EDX) reveal that this composition-driven L21 â B2 transformation is accompanied by phase segregation at the nanoscale. As a result, the Fe2-x Mn1+x Al films that show exchange-bias (x = 0, 0.25) are heterogeneous, with nanograins of an Fe-rich phase embedded in a Mn-rich matrix (a non-negative matrix factorisation algorithm was used to give an indication of the phase composition from EDX data). Our comparative analysis of XRD, magnetometry and X-ray magnetic circular dichroism (XMCD), shows that the Fe-rich nanograins and Mn-rich matrix are composed of a ferromagnetic L21 phase and an antiferromagnetic B2 phase, respectively, thus revealing that exchange-coupling between these two phases is the cause of the exchange-bias effect. Our work should inspire the development of single-layer, environmentally friendly spin valve devices based on nanocomposite Heusler films.
RESUMO
Heat pumps based on magnetocaloric and electrocaloric working bodies-in which entropic phase transitions are driven by changes of magnetic and electric field, respectively-use displaceable fluids to establish relatively large temperature spans between loads to be cooled and heat sinks1,2. However, the performance of prototypes is limited because practical magnetocaloric working bodies driven by permanent magnets3-5 and electrocaloric working bodies driven by voltage6-16 display temperature changes of less than 3 kelvin. Here we show that high-quality multilayer capacitors of PbSc0.5Ta0.5O3 display large electrocaloric effects over a wide range of starting temperatures when the first-order ferroelectric phase transition is driven supercritically (as verified by Landau theory) above the Curie temperature of 290 kelvin by electric fields of 29.0 volts per micrometre. Changes of temperature in the large central area of the capacitor peak at 5.5 kelvin near room temperature and exceed 3 kelvin for starting temperatures that span 176 kelvin (complete thermalization would reduce these values from 5.5 to 3.3 kelvin and from 176 to 73 kelvin). If magnetocaloric working bodies were to be replaced with multilayer capacitors of PbSc0.5Ta0.5O3, then the established design principles behind magnetocaloric heat pumps could be repurposed for better performance without bulky and expensive permanent magnets.