Fifty-Six Years after Acrylic Hemiarthroplasty and after Then: A Case Report of Revision THA.

We revised an acrylic femoral hip prosthesis to a total hip prosthesis for an 86-year-old female. The implant was made of dental resin and had functioned for 56 years in situ, though its stem had broken. Because of no osteolytic reaction, the reconstruction was relatively easy. From the result of histologic and radiologic examination, the bio-inertness of material and uncemented fixation seemed to contribute the minimum bone loss and to the favorite spontaneous arthrodesis after providing good joint function in her middle age.

In vivo change of elastic property in polyethylene acetabular components.

Polyethylene is an elastic material. It is known that oxidative degradation of polyethylene occurs after sterilization by means of gamma irradiation. However, there have been few detailed reports with regard to the effects of this degradation on the mechanical property, especially in total hip prostheses. The purpose of this study was to examine the change in mechanical property of irradiated and non-irradiated polyethylene cups after implantation. Fifty-six ultra-high molecular-weight polyethylene (UHMWPE) cups retrieved at revision surgery were evaluated. Thirty-two cups were sterilized by gamma irradiation in air and 24 by ethylene oxide gas (EtO). To evaluate the mechanical property of the cup and its regional distribution, Vickers hardness was measured at nine points at the cross-section of the cups. In the irradiated cups, the hardness increased in proportion to the time from sterilization. This phenomenon was not found in the cups sterilized by EtO. Less change of hardness was observed in the cups sterilized by EtO than in those sterilized by irradiation. The gamma-irradiation in air actually affected the elastic property of cup polyethylene in vivo, although any difference in the wear rate was not detected between two sterilization methods. In cases with accelerated wear of the acetabular cup, other factors affecting wear should also be considered.

Frictional torque and wear of retrieved hip prostheses: a comparison between alumina/PE and Co-Cr/PE prostheses.

Frictional torque and wear were measured in 67 retrieved cups with internal diameters of 32 mm. Thirty cups were combined with alumina heads and 37 were combined with metal heads. A lower prevalence of cup loosening was observed in alumina-polyethylene implants than in metal-polyethylene implants. No relation between frictional torque and stability of implants was detected for either type, whereas retrieved cups of alumina-polyethylene implants showed lower frictional torque than those of metal-polyethylene implants. Less wear was observed in the cups of alumina-polyethylene implants (0.13 mm/y) than in those of metal-polyethylene implants (0.19 mm/y). Less wear was observed in cups without loosening than in those with loosening in both types. These results suggest that wear has a greater influence on the stability of cups than frictional torque.