Production of Graft Copolymers of Cod Collagen with Butyl Acrylate and Vinyl Butyl Ether in the Presence of Triethylborane-Prospects for Use in Regenerative Medicine.

Collagen is a suitable material for regenerative medicine because it is characterized by its good biocompatibility. However, due to its fibrillar structure, it cannot organize itself into three-dimensional porous structures without additional modification. The introduction of synthetic monomer elements into the collagen macromolecules is a technique used to form three-dimensional, collagen-based, branched, and crosslinked structures. New types of graft copolymers made from cod collagen with a butyl acrylate and vinyl butyl ether copolymer in aqueous dispersion were obtained in the presence of triethylborane by a radical mechanism. The process of graft copolymer formation proceeded as usual by radical initiation, through radicals formed during triethylborane oxidation by oxygen residues, collagen borination, and reversible inhibition with the participation of a boroxyl radical. The characteristics of the graft copolymers were determined using methods of physical and chemical analysis (GPC, SEM, IR spectroscopy, etc.), while the cytotoxicity was assessed using the MTT assay method. It is shown that the grafting of alternating blocks of butyl acrylate and vinyl butyl ether to the protein macromolecules results in changes in the morphological pattern of the graft co-polymer in comparison with native collagen. This is manifested in the development of consolidations around the collagen fibers of the structural matrices, with the co-polymer cellular structure consisting of interpenetrating pores of unequal size. Additionally, it is important that the graft co-polymer solutions are not toxic at a certain concentration. The above properties confirm the promising nature of the technique's application as the basis for producing new materials for regenerative medicine.

Scaffold Chemical Model Based on Collagen-Methyl Methacrylate Graft Copolymers.

Polymerization of methyl methacrylate (MMA) in aqueous collagen (Col) dispersion was studied in the presence of tributylborane (TBB) and p-quinone: 2,5-di-tert-butyl-p-benzoquinone (2,5-DTBQ), p-benzoquinone (BQ), duroquinone (DQ), and p-naphthoquinone (NQ). It was found that this system leads to the formation of a grafted cross-linked copolymer. The inhibitory effect of p-quinone determines the amount of unreacted monomer, homopolymer, and percentage of grafted poly(methyl methacrylate) (PMMA). The synthesis combines two approaches to form a grafted copolymer with a cross-linked structure-"grafting to" and "grafting from". The resulting products exhibit biodegradation under the action of enzymes, do not have toxicity, and demonstrate a stimulating effect on cell growth. At the same time, the denaturation of collagen occurring at elevated temperatures does not impair the characteristics of copolymers. These results allow us to present the research as a scaffold chemical model. Comparison of the properties of the obtained copolymers helps to determine the optimal method for the synthesis of scaffold precursors-synthesis of a collagen and poly(methyl methacrylate) copolymer at 60 °C in a 1% acetic acid dispersion of fish collagen with a mass ratio of the components collagen:MMA:TBB:2,5-DTBQ equal to 1:1:0.015:0.25.

Graft Polymerization of Acrylamide in an Aqueous Dispersion of Collagen in the Presence of Tributylborane.

Graft copolymers of collagen and polyacrylamide (PAA) were synthesized in a suspension of acetic acid dispersion of fish collagen and acrylamide (AA) in the presence of tributylborane (TBB). The characteristics of the copolymers were determined using infrared spectroscopy and gel permeation chromatography (GPC). Differences in synthesis temperature between 25 and 60 °C had no significant effect on either proportion of graft polyacrylamide generated or its molecular weight. However, photomicrographs taken with the aid of a scanning electron microscope showed a breakdown of the fibrillar structure of the collagen within the copolymer at synthesis temperatures greater than 25 °C. The mechanical properties of the films and the cytotoxicity of the obtained copolymer samples were studied. The sample of a hybrid copolymer of collagen and PAA obtained at 60 °C has stronger mechanical properties compared to other tested samples. Its low cytotoxicity, when the monomer is removed, makes materials based on it promising in scaffold technologies.

Enzymatic Hydrolysis of Marine Collagen and Fibrinogen Proteins in the Presence of Thrombin.

: Enzymatic hydrolysis of native collagen and fibrinogen was carried out under comparable conditions at room temperature. The molecular weight parameters of proteins before and after hydrolysis by thrombin were monitored by gel-penetrating chromatography (GPC). An analysis of the experiment results shows that the molecular weight parameters of the initial fibrinogen (Fn) and cod collagen (CC) are very similar. High molecular CC decays within the first minute, forming two low molecular fractions. The main part (~80%) falls on the fraction with a value of Mw less than 10 kDa. The initial high molecular fraction of Fn with Mw ~320-340 kDa is not completely hydrolyzed even after three days of control. The presence of low molecular fractions with Mw ~17 and Mw ~10 kDa in the solution slightly increases within an hour and noticeably increases for three days. The destruction of macromolecules of high molecular collagen to hydrolysis products appears almost completely within the first minute mainly to the polymer with Mw ~10 kDa, and enzymatic hydrolysis of fibrinogen proceeds slower than that of collagen, but also mainly to the polymer with Mw ~10 kDa. Comparative photos of the surfaces of native collagen, fibrinogen and the scaffold based on them were obtained.