Comprehensive Study of Zr-Doped Ni-Rich Cathode Materials Upon Lithiation and Co-Precipitation Synthesis Steps.

Ni-rich layered oxides LiNi1-x-yMnxCoyO2 (NMC811, x = 0.1 and y = 0.1) are considered promising cathode materials in lithium-ion batteries (LiBs) due to their high energy density. However, those suffer a severe capacity loss upon cycling at high delithiated states. The loss of performance over time can be retarded by Zr doping. Herein, a small amount of Zr is added to NMC811 material via two alternative pathways: during the formation of the transition metal (TM) hydroxide precursor at the co-precipitation step (0.1%-Zr-cp) and during the lithiation at the solid-state synthesis step (0.1%-Zr-ss). In this work, the crystallographic Zr uptake in both 0.1%-Zr-ss and 0.1%-Zr-cp is determined and quantified through synchrotron X-ray diffraction and X-ray absorption spectroscopy. We prove that the inclusion of Zr in the TM site for 0.1%-Zr-cp leads to an improvement of both specific capacity (156 vs 149 mAh/g) and capacity retention (85 vs 82%) upon 100 cycles compared to 0.1%-Zr-ss where the Zr does not diffuse into the active material and forms only an extra phase separated from the NMC811 particles.

The effect of the pyrolysis temperature and biomass type on the biocarbons characteristics.

The conversion of biomass and natural wastes into carbon-based materials for various applications such as catalysts and energy-related materials is a fascinating and sustainable approach emerged during recent years. Precursor nature and characteristics are complex, hence, their effect on the properties of resulting materials is still unclear. In this work, we have investigated the effect of different precursors and pyrolysis temperature on the properties of produced carbon materials and their potential application as negative electrode materials in Li-ion batteries. Three biomasses, lignocellulosic brewery spent grain from a local brewery, catechol-rich lignin and tannins, were selected for investigations. We show that such end-product carbon characteristic as functional and elemental composition, porosity, specific surface area, defectiveness level, and morphology strictly depend on the precursor composition, chemical structure, and pyrolysis temperature. The electrochemical characteristics of produced carbon materials correlate with the characteristics of the produced materials. A higher pyrolysis temperature is shown to be favourable for production of carbon material for the Li-ion battery application in terms of both specific capacity and long-term cycling stability.