RESUMO
A simple route towards nanostructured mesoporous Indium-Tin Oxide (templated nano-ITO) electrodes exhibiting both high conductivities and optimized bicontinuous pore-solid network is reported. The ITO films are first produced as an X-ray-amorphous, high surface area material, by adapting recently established template-directed sol-gel methods using Sn(IV) and In(III) salts. Carefully controlled temperature/atmosphere treatments convert the as-synthesized ITO films into nano-crystalline coatings with the cubic bixbyite structure. Specially, a multi-layered synthesis was successfully undertaken for tuning the film thickness. In order to evaluate the performances of templated nano-ITO as an electrode substrate for photoelectrochemical applications, photoelectrodes were prepared by covalent grafting of a redox-active dye, the complex [Ru(bpy)2(4,4'-(CH2PO3H2)2-bpy)]Cl21 (bpy=bipyridine). Surface coverage was shown to increase with the film thickness, from 0.7 × 10-9 mol.cm-2 (one layer, 45 nm) to 3.5 × 10-9 mol.cm-2 (ten layers, 470 nm), the latter value being ~ 100 times larger than that for commercially available planar ITO. In the presence of an electron mediator, photocurrents up to 50 µA.cm-2 have been measured under visible light irradiation, demonstrating the potential of this new templated nano-ITO preparation for the construction of efficient photoelectrochemical devices.
RESUMO
This critical review presents a discussion on the major advances in the field of organic-inorganic hybrid membranes for fuel cells application. The hybrid organic-inorganic approach, when the organic part is not conductive, reproduces to some extent the behavior of Nafion where discrete hydrophilic and hydrophilic domains are homogeneously distributed. A large variety of proton conducting or non conducting polymers can be combined with various functionalized, inorganic mesostructured particles or an inorganic network in order to achieve high proton conductivity, and good mechanical and chemical properties. The tuning of the interface between these two components and the control over chemical and processing conditions are the key parameters in fabricating these hybrid organic-inorganic membranes with a high degree of reproducibility. This dynamic coupling between chemistry and processing requires the extensive use and development of complementary ex situ measurements with in situ characterization techniques, following in real time the molecular precursor solutions to the formation of the final hybrid organic-inorganic membranes. These membranes combine the intrinsic physical and chemical properties of both the inorganic and organic components. The development of the sol-gel chemistry allows a fine tuning of the inorganic network, which exhibits acid-based functionalized pores (-SO(3)H, -PO(3)H(2), -COOH), tunable pore size and connectivity, high surface area and accessibility. As such, these hybrid membranes containing inorganic materials are a promising family for controlling conductivity, mechanical and chemical properties (349 references).