Residual Stress and Tribological Performance of ZrN Coatings Produced by Reactive Bipolar Pulsed Magnetron Sputtering.

In the past few decades, ZrN thin films have been identified as wear resistant coatings for tribological applications. The mechanical and tribological properties of ZrN thin layers depend on internal stress induced by the adopted deposition techniques and deposition parameters such as pressure, temperature, and growth rate. In sputtering deposition processes, the selected target voltage waveform and the plasma characteristics also play a crucial influence on physical properties of produced coatings. In present work, ZrN thin films, obtained setting different values of duty cycle in a reactive bipolar pulsed dual magnetron sputtering plant, were investigated to evaluate their residual stress through the substrate curvature method. A considerable progressive increase of residual stress values was measured at decreasing duty cycle, attesting the significant role of voltage waveform in stress development. An evident correlation was also highlighted between the values of the duty cycle and those of wear factor. The performed analysis attested an advantageous effect of internal stress, having the samples with high compressive stress, higher wear resistance. A downward trend for wear rate with the increase of internal residual stress was observed. The choice of suitable values of duty cycle allowed to produce ceramic coatings with improved tribological performance.

In situ growth of well-dispersed CdS nanocrystals in semiconducting polymers.

A straight synthetic route to fabricate hybrid nanocomposite films of well-dispersed CdS nanocrystals (NCs) in poly[2-methoxy-5-(2'-ethyl-hexyloxy)-1,4-phenylene vinylene] (MEH-PPV) is reported. A soluble cadmium complex [Cd(SBz)2]2·MI, obtained by incorporating a Lewis base (1-methylimidazole, MI) on the cadmium bis(benzyl)thiol, is used as starting reagent in an in situ thermolytic process. CdS NCs with spherical shape nucleate and grow well below 200°C in a relatively short time (30 min). Photoluminescence spectroscopy measurements performed on CdS/MEH-PPV nanocomposites show that CdS photoluminescence peaks are totally quenched inside MEH-PPV, if compared to CdS/PMMA nanocomposites, as expected due to overlapping of the polymer absorption and CdS emission spectra. The CdS NCs are well-dispersed in size and homogeneously distributed within MEH-PPV matrix as proved by transmission electron microscopy. Nanocomposites with different precursor/polymer weight ratios were prepared in the range from 1:4 to 4:1. Highly dense materials, without NCs clustering, were obtained for a weight/weight ratio of 2:3 between precursor and polymer, making these nanocomposites particularly suitable for optoelectronic and solar energy conversion applications.

Light-emitting nanocomposite CdS-polymer electrospun fibres via in situ nanoparticle generation.

We report on the simple, in situ generation of CdS nanocrystals inside electrospun polymer fibres by thermal decomposition of a cadmium thiolate precursor, leading to nanocomposite light-emitting fibres. The modifications induced in the precursor by the thermal decomposition are investigated by a morphological, structural and spectroscopic analysis of the resulting nanocomposite fibres. This approach allows us to overcome nanofabrication difficulties related to disfavoured micro- or nanofluidic molecular flow as given by the direct incorporation of particles in the electrospinning solution. This method therefore enables the synthesis of luminescent, CdS-based composite fibres with emission peaked in the visible range, suitable as building blocks for nanophotonic devices based on light-emitting nanomaterials.

The effect of polymer matrices in the in-situ CdS formation under UV irradiation of precursor-polymer films.

Polymer films embedding cadmium thiolate precursors have been irradiated with ultraviolet laser pulses resulting in the formation of cadmium sulfide crystalline nanoparticles through a macroscopically non-destructive procedure for the host matrix. Controlling the number of the incident laser pulses, the gradual increase of the size of the nanoparticles is accomplished, and consequently the progressive change of the emission characteristics of the formed nanocomposites. The X-ray diffraction and transmission electron microscopy measurements were used for the full characterization of the nanoparticles. This study compares two polymer matrices, poly(methyl methacrylate) and a cyclic olefin copolymer, and reveals the importance of each one for the emission characteristics of the formed cadmium sulfide nanocrystals. It is found that the poly(methyl methacrylate) matrix contributes to the increase of the trap states on the surface of the formed nanocrystals, causing the broadening of their emission. On the other hand the cadmium sulfide nanoparticles, grown into the cyclic olefin copolymer matrix, exhibit narrower emission spectra.

Controlled nucleation and growth of CdS nanoparticles in a polymer matrix.

In-situ synchrotron X-ray diffraction (XRD) was used to monitor the thermal decomposition (thermolysis) of Cd thiolates precursors embedded in a polymer matrix and the nucleation of CdS nanoparticles. A thiolate precursor/polymer solid foil was heated to 300 degrees C in the X-ray diffraction setup of beamline W1.1 at Hasylab, and the diffraction curves were each recorded at 10 degrees C. At temperatures above 240 degrees C, the precursor decomposition is complete and CdS nanoparticles grow within the polymer matrix forming a nanocomposite with interesting optical properties. The nanoparticle structural properties (size and crystal structure) depend on the annealing temperature. Transmission electron microscopy (TEM) and photoluminescence (PL) analyses were used to characterize the nanoparticles. A possible mechanism driving the structural transformation of the precursor is inferred from the diffraction features arising at the different temperatures.