Sub-10 nm indium metal nanoparticles (In NPs) stabilized on conductive carbon were reacted with silver nitrate in dark conditions in water at room temperature in a galvanic replacement manner to produce an indium hydroxide/silver/carbon nanocomposite (In(OH)3/Ag/C). The chosen carbon imparted colloidal stability, high surface area, and water dispersibility suitable for photodegradation of harmful dyes in water. The size and shape of indium hydroxide and silver nanoparticles produced were found to be 6.6 ± 0.9 nm, similar to that of the In NPs that were started with. The nanocomposite was characterized by transmission electron microscopy, energy dispersive X-ray spectroscopy, powder X-ray diffraction, and thermogravimetric analysis. The galvanic reaction between In NPs and silver nitrate was tracked with UV-vis spectroscopy in a control experiment without a carbon substrate to confirm that the reaction was indeed thermodynamically spontaneous as indicated by the positive electromotive force (EMF) of +1.14 V calculated for In/Ag+ redox couple. The photocatalytic performance of the nanocomposite was evaluated to be approximately 90% under UVC radiation when 10 ppm of methylene blue and 13 wt % of indium hydroxide/silver loading on carbon were used.
RESUMO
Sago pith cellulose nanofibril (SPCNF) aerogel derived from sago pith waste (SPW) was successfully produced through three consecutive steps, namely dewaxing and delignification, ultra-sonication and homogenization and freeze drying. The aerogel was characterized using field emission scanning electron microscopy (FE-SEM), Fourier-transform infra-red spectroscopy (FTIR), X-ray diffraction (XRD) and thermogravimetric analysis (TGA). Results of the analyses collectively showed that lignin & hemicellulose were absent in the SPCNF aerogel product which has a high crystallinity index of 88%. The diameters of individual nanofibril constituents of the SPCNF were between 15 and 30 nm and aspect ratios >1000 were observed. The SPCNF aerogel, with a density measured at 2.1 mg/cm3, was efficient in methylene blue (MB) removal with a maximum MB adsorption of 222.2 mg/g at 20 °C. The adsorption of MB onto the SPCNF aerogel was rapid and found to follow a pseudo-second-order kinetic model with the adsorption isotherm being in congruence with the Langmuir model. The SPCNF aerogel exhibited outstanding MB removal efficacies with 5 mg and 20 mg of SPCNF capable of removing over 90% and almost 99% MB, respectively. The optimized pH value and temperature for MB adsorption were determined as pH 7 and 20 °C.