RESUMO
The reason to use post is to retain the core that holds the definitive prosthesis. The maxillary central incisor always poses a challenge during reconstruction using the post and core system. Dentapreg PINPost, a pre-cured flexible post made of fiber-reinforced composite (FRC), has many advantages over metallic posts and fiber posts. The purpose of this case report is to present an innovative technique to place both FRC posts and FRC sheets as a single assembly into the canal which gives a monoblock effect. This technique is feasible and may eradicate some of the problems associated with the failure of the post and core.
RESUMO
Introduction: Success of endodontic treatment relies on minimizing microbial load by chemo-mechanical preparation and intra-canal medication(ICM). Calcium hydroxide based ICMs have known disadvantages. Calcium silicate-based cements(CSC) exhibit antibacterial activity, thus promoting researchers to experiment with their formulations to use them as ICMs. Aim: Evaluation and comparison of the antimicrobial efficacy of two experimental CSC (MTA & Biodentine + 2%chlorhexidine) and Bio-C Temp against E.faecalis. Methods and Material: Test materials were divided into four groups namely Group1-Bio-C Temp, Group2-UltraCAL XS, Group3-Biodentine+2%CHX and Group4-MTA+2%CHX. Direct contact test was done by placing a standardized suspension of E.faecalis on test materials and bacterial growth was assessed spectrophotometrically using ELISA at one, three and seven days. Statistical Analysis: Data was analysed using one-way ANOVA, Tukey's multiple post hoc test and paired-t test. Results: Intragroup comparison revealed decreased mean optical density(OD) in groups 1, 2, and 4; no significant difference in group 3. Intergroup comparison showed statistical differences in mean OD values between groups (3 and 4); groups (1 and 2) at days one(p-0.018) and three(p-0.035), but no difference individually. Group 4 showed the highest antimicrobial efficacy on day seven. Conclusion: MTA+2%CHX & Biodentine+2%CHX showed better antimicrobial efficacy and hence could be used as potential ICMs.
RESUMO
Aims: The aim was the study was to evaluate and compare the mechanical properties of ACTIVA Bioactive Base/Liner (ABBL) enhanced with phytosynthesized titanium dioxide nanoparticles (nTiO2) and nano-curcumin (nCur). Methodology: Thirty samples each of ABBL (Group 1), ABBL + nTiO2 (Group 2), and ABBL + nCur (Group 3) were prepared for testing the compressive strength (CS) and flexural strength (FS). Forty-five cylinders (15 per group) (6 mm × 4 mm) were fabricated for CS and 45 for three-point bending FS measurements (22 mm × 2 mm × 2 mm). They were tested in a universal testing machine at a crosshead speed of 0.5 mm/min for CS and 0.5 mm/min with 20 mm space between the two supports for FS measurements. Statistical Analysis: Intergroup comparison of CS and FS was assessed using one-way ANOVA. The level of significance was set at 0.05. Results: Intergroup comparison showed an overall significant difference (P = 0.016 for CS) and (P = 0.001 for FS), where Group 1 had the highest and Gr 3 the least strength. No significant difference was observed between Group 1 and Group 2, while Group 3 showed significantly low strength when compared to Group 1. Conclusions: ABBL + 3% nTiO2 showed nonsignificant decrease while ABBL + 7% nCur showed significant decrease in mechanical properties.