Electron-beam induced damage process for Ca2Na2Nb5O16nanosheets.

Dielectric two-dimensional oxide nanosheets are attractive because of their thermal stability and high-k property. However, their atomic structure characterization has been limited since they are easily degraded by electron-beams. This study aimed to investigate the electron-beam induced damage mechanisms for exfoliated Ca2Na2Nb5O16(CNNO) nanosheets. Knock-on damage dominantly occurred at high voltages, leaving short-range order in the final amorphous structure. On the other hand, a series of chemical reactions predominantly occurred at low voltages, resulting in random elemental loss and a fully disordered amorphous structure. This radiolysis was facilitated by insulated CNNO nanosheets that contained a large number of dangling bonds after the chemical solution process. The radiolysis damage kinetics was faster than knock-on damage and induced more elemental loss. Based on our understanding of the electron beam-induced degradation, atomic-scale imaging of the CNNO nanosheets was successfully performed using Cs-corrected scanning transmission electron microscopy at 300 keV with a decreased beam current. This result is of particular significance because understanding of electron-beam damage in exfoliated and insulating 2D oxide sheets could improve identification of their atomic structure using electron microscopy techniques and lead to a practical guide for further extensive characterization of doped elements and layered structures to improve their properties.

Atomically sculptured heart in oxide film using convergent electron beam.

We demonstrate a fabrication of an atomically controlled single-crystal heart-shaped nanostructure using a convergent electron beam in a scanning transmission electron microscope. The delicately controlled e-beam enable epitaxial crystallization of perovskite oxide LaAlO3 grown out of the relative conductive interface (i.e. 2 dimensional electron gas) between amorphous LaAlO3/crystalline SrTiO3.

Influence of combinatory effects of STEM setups on the sensitivity of differential phase contrast imaging.

Differential phase-contrast (DPC) imaging in the scanning transmission electron microscopy (STEM) mode has been suggested as a new method to visualize the nanoscale electromagnetic features of materials. However, the quality of the DPC image is very sensitive to the electron-beam alignment, microscope setup, and specimen conditions. Unlike normal STEM imaging, the microscope setup variables in the DPC mode are not independent; rather, they are correlated factors decisive for field sensitivity. Here, we systematically investigated the independent and combinatory effects of microscope setups on the sensitivity of the DPC image in a hard magnet, Nd2Fe14B alloy. To improve sensitivity, a smaller overlap of the electron beam with annular detectors and a greater camera length were required. However, these factors cannot be controlled independently in the two-condenser-lens system. In this linked system, the effect of the camera length on the DPC sensitivity was slightly more predominant than the overlap. Furthermore, the DPC signal was noisy and scattered at a small overlap of less than 11%. The electron-beam current does not evidently affect the sensitivity. In addition, the DPC sensitivity was examined with respect to the sample thickness, and the optimum thickness for high sensitivity was approximately 65 nm for the hard magnetic material Nd2Fe14B. This practical approach to the STEM setup and sample thickness may provide experimental guidelines for further application of the DPC analysis method.

Single-Layer Graphene-Based Transparent and Flexible Multifunctional Electronics for Self-Charging Power and Touch-Sensing Systems.

Applications in the field of portable and wearable electronics are becoming multifunctional, and the achievement of transparent electronics extensively expands the applications into devices such as wearable flexible displays or skin-attachable mobile computers. Moreover, the self-charging power system (SCPS) is the core technique for realizing portable and wearable electronics. Here, we propose a transparent and flexible multifunctional electronic system in which both an all-in-one SCPS and a touch sensor are combined. A single-layer graphene (SLG) film was adapted as an electrode for the supercapacitor, touch sensor, and a triboelectric nanogenerator (TENG), thus making an electronic system that is ultrathin, lightweight, transparent, and flexible. Capacitive-type transparent and flexible electronic devices can be simultaneously used as an electrochemical double-layer capacitance-based supercapacitor and as a sensitive, fast-responding touch sensor in a single-device architecture by inserting a separator of polyvinyl alcohol-lithium chloride-soaked polyacrylonitrile electrospun mat on polyethylene naphthalate between two symmetric SLG film electrodes. Furthermore, a transparent all-in-one SCPS was fabricated by laminating a TENG device with a supercapacitor, and high-performance electric power generation/storage capability is demonstrated.

High strength nanostructured Al-based alloys through optimized processing of rapidly quenched amorphous precursors.

We report the methods increasing both strength and ductility of aluminum alloys transformed from amorphous precursor. The mechanical properties of bulk samples produced by spark-plasma sintering (SPS) of amorphous Al-Ni-Co-Dy powders at temperatures above 673 K are significantly enhanced by in-situ crystallization of nano-scale intermetallic compounds during the SPS process. The spark plasma sintered Al84Ni7Co3Dy6 bulk specimens exhibit 1433 MPa compressive yield strength and 1773 MPa maximum strength together with 5.6% plastic strain, respectively. The addition of Dy enhances the thermal stability of primary fcc Al in the amorphous Al-TM -RE alloy. The precipitation of intermetallic phases by crystallization of the remaining amorphous matrix plays important role to restrict the growth of the fcc Al phase and contributes to the improvement of the mechanical properties. Such fully crystalline nano- or ultrafine-scale Al-Ni-Co-Dy systems are considered promising for industrial application because their superior mechanical properties in terms of a combination of very high room temperature strength combined with good ductility.

Cross-sectional analysis of W-cored Ni nanoparticle via focused ion beam milling with impregnation.

Tungsten and nickel bimetallic nanoparticle is synthesized by radio frequency thermal plasma process which belongs to the vapor phase condensation technology. The morphology and chemical composition of the synthesized particle were investigated using the conventional nanoparticle transmission electron microscopy (TEM) sample. A few part of them looked like core/shell structured particle, but ambiguities were caused by either TEM sample preparation or TEM analysis. In order to clarify whether a core/shell structure is developed for the particle, various methodologies were tried to prepare a cross-sectional TEM sample. Focused ion beam (FIB) milling was conducted for cold-compacted particles, dispersed particles on silicon wafer, and impregnated particles with epoxy which is compatible with electron beam. A sound cross-sectional sample was just obtained from cyanoacrylate impregnation and FIB milling procedure. A tungsten-cored nickel shell structure was precisely confirmed with aid of cross-sectional sample preparation method.