RESUMO
Fluorinated electrolytes based on fluoroethylene carbonate (FEC) have been considered as promising alternative electrolytes for high-voltage and high-energy capacity lithium-ion batteries (LIBs). However, the compatibility of the fluorinated electrolytes with graphite negative electrodes is unclear. In this paper, we have systematically investigated, for the first time, the stability of fluorinated electrolytes with graphite negative electrodes, and the result shows that unlike the ethylene carbonate (EC)-based electrolyte, the FEC-based electrolyte (EC was totally replaced by FEC) is incapable of forming a protective and effective solid electrolyte interphase (SEI) that protects the electrolyte from runaway reduction on the graphite surface. The reason is that the lowest unoccupied molecular orbital energy levels are also lowered by the introduction of fluorine into the solvent, and the FEC solvent has poorer resistance against reduction, leading to instability on the graphite negative electrode. To tackle this problem, two lithium salts of lithium bis(oxalato)borate and lithium difluoro(oxalato)borate (LiDFOB) have been investigated as negative-electrode film-forming additives. Incorporation of only 0.5 wt % LiDFOB to a FEC-based electrolyte [1.0 M LiPF6 in 3:7 (FEC-ethyl methyl carbonate)] results in excellent cycling performance of the graphite negative electrode. This improved property originates from the generation of a thinner and better quality SEI film with little LiF by the sacrificial reduction of the LiDFOB additive on the graphite negative electrode surface. On the other hand, this additive can stabilize the electrolyte by scavenging HF. Meanwhile, the incorporated LiDFOB additive has positive influence on the interphase layer on the positive electrode surface and significantly decreases the amount of HF formation, finally leading to improved cycling stability and rate capability of LiNi0.5Mn1.5O4 electrodes at a high cutoff voltage of 5 V. The data demonstrate that the LiDFOB additive not only exhibits a superior compatibility with graphite but also improves the electrochemical properties of high-voltage spinel LiNi0.5Mn1.5O4 positive electrodes considerably, confirming its potential as a prospective, multifunctional additive for 5 V fluorinated electrolytes in high-energy capacity lithium-ion batteries (LIBs).
RESUMO
Rechargeable batteries made from low-cost and abundant materials operating in safe aqueous electrolytes are attractive for large-scale energy storage. Sodium-ion battery is considered as a potential alternative of current lithium-ion battery. As sodium-intercalation compounds suitable for aqueous batteries are limited, we adopt a novel concept of Li(+)/Na(+) mixed-ion electrolytes to create two batteries (LiMn2O4/Na0.22MnO2 and Na0.44MnO2/TiP2O7), which relies on two electrochemical processes. One involves Li(+) insertion/extraction reaction, and the other mainly relates to Na(+) extraction/insertion reaction. Two batteries exhibit specific energy of 17 Wh kg(-1) and 25 Wh kg(-1) based on the total weight of active electrode materials, respectively. As well, aqueous LiMn2O4/Na0.22MnO2 battery is capable of separating Li(+) and Na(+) due to its specific mechanism unlike the traditional "rocking-chair" lithium-ion batteries. Hence, the Li(+)/Na(+) mixed-ion batteries offer promising applications in energy storage and Li(+)/Na(+) separation.