The grain-refining mechanism with minor Sr - Sc - La and ultrasonic vibration treatment (UVT) in the hypereutectic Al-20Si alloy were studied. The results demonstrated that the microstructure of the hypereutectic Al-20Si alloy could be refined significantly, further improve its mechanical properties. The desirable refinement of the microstructure was achieved using 0.2% Sr, 0.15% Sc, and 0.3% La under UVT, achieving the highest grain circularity coefficient, hardness, elongation, and area reduction. The tensile strength was the largest with the addition of 0.2% La. The findings of this study provide theoretical and experimental guidelines for the fabrication of structural materials for application in automotive, aerospace, and deep-sea equipment.
RESUMO
2-O-α-D-Glucosyl glycerol (2-αGG) can be used as a multipurpose anti-aging, cell-stimulating, and skin moisturizing agent in the cosmetic industry. Sucrose phosphorylase (SPase) has been widely used in the production of 2-αGG. In this paper, the gene encoding sucrose phosphorylase from Bifidobacterium longum (BlSP) was inserted into pRSF-Duet-1 to construct the recombinant plasmid pRSF-BlSP and was functionally expressed in E. coli BL21(DE3) to be used as a biocatalyst for the synthesis of 2-αGG firstly. The mutations of BlSP were carried out based on alanine scanning, and a positive mutant G293A with a 50% increase in activity for 2-αGG production was identified. Mutant G293A has less Km and bigger kcat/Km towards glycerol than the parental BlSP. Subsequently, the production of 177.6 g/L 2-αGG was attained from 1 M sucrose and 1.2 M glycerol catalyzed by 17 mg/mL G293A mutant. This study indicated that BlSP has good potential in the production of 2-αGG.