The remediation potential and kinetics of Pb2+ adsorbed by the organic frameworks of Cladophora rupestris.

Cladophora rupestris is ubiquitous in many kinds of waterbodies, and C. rupestris biomass can serve as a carrier for adsorbing and transferring heavy metals. Batch experiments and characterization were performed. Results showed that the organic frameworks of C. rupestris (CROF) had a specific surface area of 2.58 m2/g and an external surface area of 2.06 m2/g. Many mesopores were present in CROF, mainly distributed in 2.5-7.5 nm. The zeta potentials were within the range of - 4.46 to - 13.98 mV in the tested pH of 2.0-9.0. CROF could effectively adsorb Pb2+ in large pH range. The maximum adsorption capacity (qmax) of Pb2+ on CROF was 15.02 mg/g, and 97% of Pb2+ was adsorbed onto CROF after 25 min. CROF had a preferential adsorption of Pb2+. The protein secondary structures and carbon skeletons of CROF all worked in adsorption. The main Pb2+ adsorption mechanisms were pore filling, electrostatic attraction, Pb-π interaction, and surface complexation. Therefore, it is valuable as a biosorbent for the removal of Pb2+ from waterbodies.

A room-temperature ultrasonic hydrogen sensor based on a sensitive layer of reduced graphene oxide.

It is challenging to increase the sensitivity of a hydrogen sensor operating at room temperature due to weak sorption and tiny mass of hydrogen. In this work, an ultrasonic sensor is presented for detecting hydrogen, which is composed of a 128° YX-LiNbO3 substrate and a reduced graphene oxide (RGO) sensitive layer with a platinum catalyzer. By optimizing the depositing parameters of RGO and platinum, a considerably high sensitivity is achieved at room temperature. A frequency shift of 308.9 kHz is obtained in 100 ppm hydrogen mixed with argon, and a frequency shift of 24.4 kHz is obtained in 1000 ppm hydrogen mixed in synthetic air. It is demonstrated that in addition to strong sorption of the sensitive layer, the coaction of mass load and conductivity variation is key to high sensitivity of the sensor. By establishing the original conductivity of the sensitive layer within the "conductivity window" for enhancing electrical response, we improve the sensitivity of the ultrasonic sensor, which is available for detecting hydrogen with an extremely low concentration of 5 ppm.