Self-assembled biobased chitosan hybrid carrying N/P/B elements for polylactide with enhanced fire safety and mechanical properties.

The inherent shortcomings such as flammability, brittleness, and low crystallinity limit the broad applications of poly(lactic acid) (PLA). To improve the fire resistance and mechanical properties of PLA, a chitosan-based core-shell flame retardant additive (APBA@PA@CS) was prepared for PLA via the self-assembly of interionic interactions among chitosan (CS), phytic acid (PA), and 3-aminophenyl boronic acid (APBA). The peak heat release rate (pHRR) and total heat release rate (THR) of PLA composite containing 3 wt% APBA@PA@CS decreased from 460.1 kW/m2 and 75.8 MJ/m2 to 419.0 kW/m2 and 53.1 MJ/m2, respectively. The presence of APBA@PA@CS contributed to the formation of a high-quality char layer rich in phosphorus and boron in the condensed phase and released non-flammable gases in the gas phase to hinder the exchange of heat and O2, thereby having a synergistic flame retardant effect. Meanwhile, the tensile strength, elongation at break, impact strength, and crystallinity of PLA/APBA@PA@CS were increased by 3.7 %, 17.4 %, 5.3 %, and 55.2 %, respectively. This study provides a feasible route to construct a chitosan-based N/B/P tri-element hybrid to improve the fire safety performance and mechanical properties of PLA biocomposites.

Flexible transparent PES/silver nanowires/PET sandwich-structured film for high-efficiency electromagnetic interference shielding.

We have developed a kind of high-yield synthesis strategy for silver nanowires by a two-step injection polyol method. Silver nanowires and polyethylene oxide (PEO) (M(w) = 900,000) were prepared in a homogeneous-coating ink. Wet composite films with different thicknesses were fabricated on a PET substrate by drawn-down rod-coating technology. Silver nanowires on PET substrates present a homogeneous distribution under the assistance of PEO. Then PEO was thermally removed in situ at a relatively low temperature attributed to its special thermal behavior under atmospheric conditions. As-prepared metallic nanowire films on PET substrates show excellent stability and a good combination of conductivity and light transmission. A layer of transparent poly(ethersulfones) (PESs) was further coated on silver nanowire networks by the same coating method to prevent the shedding and corrosion of silver nanowires. Sandwich-structured flexible transparent films were obtained and displayed excellent electromagnetic interference (EMI) shielding effectiveness.