Precise Sn-Doping Modulation for Optimizing CdWO4 Nanorod Photoluminescence.

The cadmium tungstate rods have been given much attention due to their potential for usage in numerous luminescent applications. We have prepared single crystalline Sn-doped Cd1-xSnxWO4 (where x = 0, 1, 3, and 5%) nanorods (NRDs) and characterized them using refined X-ray diffraction and TEM analysis, revealing a monoclinic phase and a crystallite size that decreased from 62 to 38 nm as Sn concentration increased. Precise Sn doping modulation in CdWO4 NRDs causes surface recombination of electrons and holes, which causes the PL intensity to decrease as the Sn content rises. The chromaticity diagram shows that an increase in the Sn content caused a change in the emission color from sky blue to light green, which was attributed to the increased defect density. The photoluminescence time decay curve of all samples fit well with double-order exponential decay, and the average decay lifetime was found to be 1.11, 0.93, and 1.16 ns for Cd1-xSnxWO4, x = 0, 1, and 5%, respectively. This work provides an understanding of the behavior of Sn-doped CdWO4 NRDs during electron transitions and the physical nature of emission that could be used in bio-imaging, light sources, displays, and other applications.

Room Temperature Magnetic Memory Effect in Cluster-Glassy Fe-doped NiO Nanoparticles.

The Fe-doped NiO nanoparticles that were synthesized using a co-precipitation method are characterized by enhanced room-temperature ferromagnetic property evident from magnetic measurements. Neutron powder diffraction experiments suggested an increment of the magnetic moment of 3d ions in the nanoparticles as a function of Fe-concentration. The temperature, time, and field-dependent magnetization measurements show that the effect of Fe-doping in NiO has enhanced the intraparticle interactions due to formed defect clusters. The intraparticle interactions are proposed to bring additional magnetic anisotropy energy barriers that affect the overall magnetic moment relaxation process and emerging as room temperature magnetic memory. The outcome of this study is attractive for the future development of the room temperature ferromagnetic oxide system to facilitate the integration of spintronic devices and understanding of their fundamental physics.

Short-Range Correlated Magnetic Core-Shell CrO2/Cr2O3 Nanorods: Experimental Observations and Theoretical Considerations.

With the evolution of synthesis and the critical characterization of core-shell nanostructures, short-range magnetic correlation is of prime interest in employing their properties to develop novel devices and widespread applications. In this regard, a novel approach of the magnetic core-shell saturated magnetization (CSSM) cylinder model solely based on the contribution of saturated magnetization in one-dimensional CrO2/Cr2O3 core-shell nanorods (NRs) has been developed and applied for the determination of core-diameter and shell-thickness. The nanosized effect leads to a short-range magnetic correlation of ferromagnetic core-CrO2 extracted from CSSM, which can be explained using finite size scaling method. The outcome of this study is important in terms of utilizing magnetic properties for the critical characterization of core-shell nanomagnetic materials.

Phonon Confinement Induced Non-Concomitant Near-Infrared Emission along a Single ZnO Nanowire: Spatial Evolution Study of Phononic and Photonic Properties.

The impact of mixed defects on ZnO phononic and photonic properties at the nanoscale is only now being investigated. Here we report an effective strategy to study the distribution of defects along the growth direction of a single ZnO nanowire (NW), performed qualitatively as well as quantitatively using energy dispersive spectroscopy (EDS), confocal Raman-, and photoluminescence (PL)-mapping technique. A non-concomitant near-infrared (NIR) emission of 1.53 ± 0.01 eV was observed near the bottom region of 2.05 ± 0.05 µm along a single ZnO NW and could be successfully explained by the radiative recombination of shallowly trapped electrons V_O^(**) with deeply trapped holes at V_Zn^''. A linear chain model modified from a phonon confinement model was used to describe the growth of short-range correlations between the mean distance of defects and its evolution with spatial position along the axial growth direction by fitting the E2H mode. Our results are expected to provide new insights into improving the study of the photonic and photonic properties of a single nanowire.