RESUMO
The utilization of agricultural and forestry residues for the development and preparation of green binderless fiberboard (BF) is an effective way to realize high-value utilization of lignocellulose biomass resources. This study focuses on the fabrication of BF with excellent mechanical and waterproof properties, utilizing poplar wood residue (PWR) as raw material and Trametes hirsuta as a pretreatment method. During the fermentation process, lignin-degrading enzymes and biological factors, such as sugars, were produced by T. hirsuta, which activated lignin by depolymerizing lignin bonds and modifying structural functional groups, and forming new covalent bonds between poplar fibers, ultimately enhancing adhesion. Additionally, the activated lignin molecules and sugar molecules coalesce under high temperatures and pressures, forming a dense carbonization layer that bolsters the mechanical properties of the fiberboard and effectively shields it from rapid water infiltration. The bio-pretreated BF for 10 days shows a MOR and MOE of up to 36.1 Mpa and 3704.3 Mpa, respectively, which is 261% and 247.8% higher than that of the bio-untreated fiberboard, and the water swelling ratio (WSR) rate is only 5.6%. Chemical composition analysis revealed that repolymerization occurred among lignin, cellulose, and hemicellulose, especially the molecular weight of lignin changed significantly, with the Mw of lignin increasing from 312066 g/mol to 892362 g/mol, and then decreasing to 825021 g/mol. Mn increased from 277790 g/mol to 316987.5 g/mol and then decreased to 283299.5 g/mol at 21 days. Compared to other artificial fiberboards prepared through microbial pretreatment, the BF prepared by microorganisms in this study exhibited the highest mechanical properties among the poplar wood biobased panels.