Molecular-weight effects of a homopolymer on the AB- and ABC-stacks of perforations in block copolymer/homopolymer films.

We have demonstrated the molecular-weight effects of adding homopolystyrene (hPS) on the evolution of perforated layers and double gyroids in polystyrene-block-poly(methyl methacrylate)-based films during isothermal annealing. Two homopolystyrenes of 2.8 and 17 kg mol-1 were used. To prepare blend films, PS-b-PMMA and hPSx (x: 2.8 or 17) were mixed at a weight-fraction ratio of 75/25 in toluene and then spin-coated at SiOx/Si. Spin coating inevitably produced films with thick edges at the periphery of the substrate. The structural evolution of the spun films was in situ characterized by grazing incidence small-angle X-ray scattering (GISAXS). The annealed films were then characterized using a scanning electron microscope (SEM). We found that thin middle regions behaved differently from thick beads for the films. The middle of the blend films mainly formed perforated layers with different spatial orders and orientations, depending on the molecular weight of added hPS chains. Hexagonally perforated layers quickly formed at 205 °C for PS-b-PMMA/hPS2.8 films. However, when hPS17 was used instead of hPS2.8, perforated layers formed with defects in PS-b-PMMA/hPS17 films annealed at 205 °C. Annealing at 240 °C improved the spatial order and orientation of perforated layers for a PS-b-PMMA/hPS17 film. Nevertheless, annealing at 240 °C inversely depressed the in-plane spatial order of perforated layers for a PS-b-PMMA/hPS2.8 film. The depression in the in-plane spatial order is ascribed to a dilution effect of added short chains. Compared to the middle regions, the thick beads went through several metastable phases, such as perpendicularly oriented perforated layers and double gyroids.

Distributions of Deuterated Polystyrene Chains in Perforated Layers of Blend Films of a Symmetric Polystyrene-block-poly(methyl methacrylate).

We have examined the spatial distributions of polymer chains in blend films of weakly segregated polystyrene-block-poly(methyl methacrylate) [P(S-b-MMA)] and deuterated polystyrene (dPS). By fine-tuning the composition (ϕPS+dPS = 63.8 vol %) of the total PS/dPS component and annealing temperature (230 and 270 °C), P(S-b-MMA)/dPS blend films mainly form perforated layers with a parallel orientation (hereafter PLs//). The distributions of dPS in PLs// were probed by grazing-incidence small-angle neutron scattering (GISANS) and time-of-flight neutron reflectivity (ToF-NR). GISANS and ToF-NR results offer evidence that dPS chains preferentially locate at the free surface and within the PS layers for blend films that were annealed at 230 °C. Upon annealing at 270 °C, dPS chains distribute within PS layers and perforated PMMA layers. Nevertheless, dPS chains still retain a surface preference for thin films. In contrast, such surface segregation of dPS chains is prohibited for thick films when annealed at 270 °C.