Visible-Light-Assisted Photoelectrochemical Biosensing of Uric Acid Using Metal-Free Graphene Oxide Nanoribbons.

In this study, we demonstrate the visible-light-assisted photoelectrochemical (PEC) biosensing of uric acid (UA) by using graphene oxide nanoribbons (GONRs) as PEC electrode materials. Specifically, GONRs with controlled properties were synthesized by the microwave-assisted exfoliation of multi-walled carbon nanotubes. For the detection of UA, GONRs were adopted to modify either a screen-printed carbon electrode (SPCE) or a glassy carbon electrode (GCE). Cyclic voltammetry analyses indicated that all Faradaic currents of UA oxidation on GONRs with different unzipping/exfoliating levels on SPCE increased by more than 20.0% under AM 1.5 irradiation. Among these, the GONRs synthesized under a microwave power of 200 W, namely GONR(200 W), exhibited the highest increase in Faradaic current. Notably, the GONR(200 W)/GCE electrodes revealed a remarkable elevation (~40.0%) of the Faradaic current when irradiated by light-emitting diode (LED) light sources under an intensity of illumination of 80 mW/cm2. Therefore, it is believed that our GONRs hold great potential for developing a novel platform for PEC biosensing.

Low-Temperature CVD Graphene Nanostructures on Cu and Their Corrosion Properties.

Chemical vapor deposition (CVD) graphene is reported to effectively prevent the penetration of outer factors and insulate the underneath metals, hence achieving an anticorrosion purpose. However, there is little knowledge about their characteristics and corresponding corrosion properties, especially for those prepared under different parameters at low temperatures. Using electron cyclotron resonance chemical vapor deposition (ECR-CVD), we can successfully prepare graphene nanostructures on copper (Cu) at temperatures lower than 600 °C. Scanning electron microscopy (SEM), X-ray diffraction (XRD), Raman spectroscopy, and potentiodynamic polarization measurements were used to characterize these samples. In simulated seawater, i.e., 3.5 wt.% sodium chloride (NaCl) solution, the corrosion current density of one graphene-coated Cu fabricated at 400 °C can be 1.16 × 10-5 A/cm², which is one order of magnitude lower than that of pure Cu. Moreover, the existence of tall graphene nanowalls was found not to be beneficial to the protection as a consequence of their layered orientation. These correlations among the morphology, structure, and corrosion properties of graphene nanostructures were investigated in this study. Therefore, the enhanced corrosion resistance in selected cases suggests that the low-temperature CVD graphene under appropriate conditions would be able to protect metal substrates against corrosion.