The effect of chlorhexidine and dimethyl sulfoxide on long-term sealing ability of two calcium silicate cements in root canal.

OBJECTIVES: To evaluate the long-term effect of chlorhexidine (CHX) and dimethyl sulfoxide (DMSO) on the sealing ability and biomineralization of two different calcium silicate cements (CSC) in root canal. METHODS: Sixty human third molar root canals were obturated with ProRoot MTA or Biodentine. Before obturation the canals were irrigated with saline (control), 2% CHX or 5% DMSO. Microleakage was tested after three days and after six months. After additional six months (12 months after root filling) the roots were cut into 2 mm thick dentine discs. The discs were stored in artificial saliva for one year. The bond strength was measured with the push-out method, and the failure mode was evaluated with a stereomicroscope. The most apical disc of each tooth was used for Vickers hardness test. RESULTS: No significant differences between the groups was found in initial microleakage. The leakage increased significantly during the 6-month storage in all groups except in Biodentine-CHX group and Biodentine-DMSO group. CHX and DMSO irrigation significantly increased the leakage with ProRoot MTA with time, but there was no statistically significant difference compared to the ProRoot MTA-control group at six months' time point. CHX significantly reduced the push-out bond strength of ProRoot MTA. With Biodentine irrigation with CHX or DMSO resulted with significantly higher push-out strength compared to the Biodentine control group. Fracture analysis showed statistically significant difference in the distribution of the fractures between the groups, but neither CHX nor DMSO change the fracture pattern statistically significantly. With Vickers hardness test ProRoot MTA with and without DMSO as the final irrigant showed significantly higher dentin hardness than any Biodentine-group. SIGNIFICANCE: Considering that aging increased the leakage in all groups except with Biodentine-DMSO and the differences in the push-out strength and surface microhardness data, it appears that the time-related biomineralizing effect of MTA and Biodentine does not improve sealing to dentin. CHX significantly reduced ProRoot MTA bond strength and increased pure adhesive failures with both cements.

The Effect of Chlorhexidine and Dimethyl Sulfoxide on Long-Term Microleakage of Two Different Sealers in Root Canals.

OBJECTIVE: The aim of root canal obturation is to prevent leakage and inhibit microbial invasion. This study aimed to determine the effect of chlorhexidine (CHX) and dimethyl sulfoxide (DMSO) as final irrigants on microleakage of root filling immediately and after 18 months. The hypothesis was that either CHX or DMSO would not affect the immediate or long-term microleakage. METHODS: A total of 120 human third molar root canals were obturated with RealSeal SE or Topseal and gutta percha. Before obturation, the canals were irrigated with saline (control), 2% CHX or 5% DMSO. Microleakage of half of each groups (n=10) was measured after 3 days, and of the other half was measured after 18 months with fluid filtration method. RESULTS: In immediate measurements, RealSeal SE performed significantly better in CHX-irrigated group (p=0.035; Mann-Whitney test). For both sealers, DMSO had the lowest mean microleakage values, which were also statistically significantly lower than with CHX irrigation within sealers (p<0.009 for Topseal and p=0.04 for RealSeal SE; Mann-Whitney test). With RealSeal SE, the microleakage with CHX was significantly higher than that in controls (p=0.022; Mann-Whitney test). CONCLUSION: Neither final irrigant showed statistically significant differences in the immediate microleakage within the two sealers. Irrigation with DMSO caused significantly less microleakage than CHX for both sealers after 18 months.