The inverted metamorphic multi-junction solar cell is anticipated to be widely applied in stratospheric flight because of its exceptional properties of flexibility and light weight. We propose an ipsilateral welding technology based on Ti/Au electrodes to simplify the fabrication process of GaInP/GaAs/InGaAs solar cells and encapsulate large-sized flexible solar cells. After annealing at 200°C for 2 h, the Ti/Au electrode achieved a low specific contact resistivity of 2.9×10-7 Ωâ c m 2. The performance of the ohmic contact remains stable after the thermal cycling tests. The Ti/Au electrode can require less heat input for welding to reduce the risk of microcrack formation of the solar cells. By employment of this electrode, a 24c m 2 solar cell achieved a conversion efficiency of 34.74%. A flexible solar cell module with an efficiency of 32.82% under AM 1.5G illumination was obtained by the ipsilateral electrode welding technology.
RESUMO
This erratum corrects an error in Fig. 1 of the original paper, Appl. Opt.63, 2815 (2024)APOPAI0003-693510.1364/AO.518102.
RESUMO
The extended damp heat and thermal cycling tests were performed on unencapsulated flexible thin-film GaInP/GaAs/InGaAs solar cells to assess the long-term stability. The solar cells were subjected to 85 °C/85% damp heat test for more than 1000 h and 420 cycles of thermal cycling test between -60 °C and 75 °C, respectively. The performance attenuations of flexible solar cells were less than 2% in both cases, which were due to the slow decline of the open-circuit voltage with aging time. The slight decrease in open voltage was attributed to the increase in reverse saturation current due to the enhanced recombination, which was in good agreement with the calculation based on the two-diode model. The good performance of the unencapsulated flexible GaInP/GaAs/InGaAs solar cells in severe environment indicated the stable and reliable device fabrication art in the experiment.