Effect of Cold Drawing and Annealing in Thermomechanical Treatment Route on the Microstructure and Functional Properties of Superelastic Ti-Zr-Nb Alloy.

In this study, a superelastic Ti-18Zr-15Nb (at. %) alloy was subjected to thermomechanical treatment, including cold rotary forging, intermediate annealing, cold drawing, post-deformation annealing, and additional low-temperature aging. As a result of intermediate annealing, two structures of ß-phase were obtained: a fine-grained structure (d ≈ 3 µm) and a coarse-grained structure (d ≈ 11 µm). Cold drawing promotes grain elongation in the drawing direction; in a fine-grained state, grains form with a size of 4 × 2 µm, and in a coarse-grained state, they grow with a size of 16 × 6 µm. Post-deformation annealing (PDA) at 550 °C for 30 min leads to grain sizes of 5 µm and 3 µm, respectively. After PDA at 550 °C (30 min) in the fine-grained state, the wire exhibits high tensile strength (UTS = 624 MPa), highest elongation to failure (δ ≥ 8%), and maximum difference between the dislocation and transformation yield stresses, as well as the highest superelastic recovery strain (εrSE ≥ 3.3%) and total elastic + superelastic recovery strain (εrel+SE ≥ 5.4%). Additional low-temperature aging at 300 °C for 30-180 min leads to ω-phase formation, alloy hardening, embrittlement, and a significant decrease in superelastic recovery strain.

Effect of High-Pressure Torsion and Annealing on the Structure, Phase Composition, and Microhardness of the Ti-18Zr-15Nb (at. %) Alloy.

The Ti-18Zr-15Nb shape memory alloys are a new material for medical implants. The regularities of phase transformations during heating of this alloy in the coarse-grained quenched state and the nanostructured state after high-pressure torsion have been studied. The specimens in quenched state (Q) and HPT state were annealed at 300-550 °C for 0.5, 3, and 12 h. The α-phase formation in Ti-18Zr-15Nb alloy occurs by C-shaped kinetics with a pronounced peak near 400-450 °C for Q state and near 350-450 °C for HPT state, and stops or slows down at higher and lower annealing temperatures. The formation of a nanostructured state in the Ti-18Zr-15Nb alloy as a result of HPT suppresses the ß→ω phase transformation during low-temperature annealing (300-350 °C), but activates the ß→α phase transformation. In the Q-state the α-phase during annealing at 450-500 °C is formed in the form of plates with a length of tens of microns. The α-phase formed during annealing of nanostructured specimens has the appearance of nanosized particle-grains of predominantly equiaxed shape, distributed between the nanograins of ß-phase. The changes in microhardness during annealing of Q-specimens correlate with changes in phase composition during aging.

Effect of Cooling and Annealing Conditions on the Microstructure, Mechanical and Superelastic Behavior of a Rotary Forged Ti-18Zr-15Nb (at. %) Bar Stock for Spinal Implants.

In this work, the microstructure, phase state, texture, superelastic and mechanical properties of a Ti-18Zr-15Nb (at. %) shape memory alloy subjected to a combined thermomechanical treatment, including hot rotary forging with either air cooling or water quenching and post-deformation annealing are studied. It was revealed that the main structural component of the deformed and annealed alloy is BCC ß-phase. With an increase in the forging temperature from 600 to 700 °C, the average grain size increases from 5.4 to 17.8 µm for the air-cooled specimens and from 3.4 to 14.7 µm for the water-quenched specimens. Annealing at 525 °C after forging at 700 °C with water quenching leads to the formation of a mixed statically and dynamically polygonized substructure of ß-phase. In this state, the alloy demonstrates the best combination of functional properties in this study: a Young's modulus of ~33 GPa, an ultimate tensile strength of ~600 MPa and a superelastic recovery strain of ~3.4%.