This paper presents the formation of magnesium aluminate spinel using composite particles prepared via electrostatic adsorption (ESA). Scanning electron microscopy (SEM) images confirmed the presence of Al2O3-MgO composite particles. A mixture of Al2O3 and MgO raw materials was also prepared by using the conventional bead-milling method for comparison. The samples sintered at elevated temperatures were characterized through X-ray diffraction, SEM, and relative density measurements. Additionally, the lattice parameter and strain of the samples were determined using the Nelson-Riley function and the Williamson-Hall equation. A pure spinel phase formed in the ESA-derived sample sintered at 1400 °C, while the MgO structure remained in the conventionally prepared sample sintered at 1600 °C. The densities of samples sintered at 1450 °C or higher exceeded 90%. The lattice strain of the prepared samples was inversely proportional to the sintering temperature, attributed to the formation of large grains at higher temperatures. However, the sample sintered at 1600 °C for 8 h exhibited the highest strain of 0.0074 because the crystals grew in a certain direction.