Determination of the in vivo degradation mechanism of PEGDA hydrogels.

Poly(ethylene glycol) (PEG) hydrogels are one of the most extensively utilized biomaterials systems due to their established biocompatibility and highly tunable properties. It is widely acknowledged that traditional acrylate-derivatized PEG (PEGDA) hydrogels are susceptible to slow degradation in vivo and are therefore unsuitable for long-term implantable applications. However, there is speculation whether the observed degradation is due to hydrolysis of endgroup acrylate esters or oxidation of the ether backbone, both of which are possible in the foreign body response to implanted devices. PEG diacrylamide (PEGDAA) is a polyether-based hydrogel system with similar properties to PEGDA but with amide linkages in place of the acrylate esters. This provides a hydrolytically-stable control that can be used to isolate the relative contributions of hydrolysis and oxidation to the in vivo degradation of PEGDA. Here we show that PEGDAA hydrogels remained stable over 12 weeks of subcutaneous implantation in a rat model while PEGDA hydrogels underwent significant degradation as indicated by both increased swelling ratio and decreased modulus. As PEGDA and PEGDAA have similar susceptibility to oxidation, these results demonstrate for the first time that the primary in vivo degradation mechanism of PEGDA is hydrolysis of the endgroup acrylate esters. Additionally, the maintenance of PEGDAA hydrogel properties in vivo indicates their suitability for long-term implants. These studies serve to elucidate key information about a widely used biomaterial system to allow for better implantable device design and to provide a biostable replacement option for PEGDA in applications that require long-term stability.

Drying and storage effects on poly(ethylene glycol) hydrogel mechanical properties and bioactivity.

Hydrogels based on poly(ethylene glycol) (PEG) are increasingly used in biomedical applications because of their ability to control cell-material interactions by tuning hydrogel physical and biological properties. Evaluation of stability after drying and storage are critical in creating an off-the-shelf biomaterial that functions in vivo according to original specifications. However, there has not been a study that systematically investigates the effects of different drying conditions on hydrogel compositional variables. In the first part of this study, PEG-diacrylate hydrogels underwent common processing procedures (vacuum-drying, lyophilizing, hydrating then vacuum-drying), and the effect of this processing on the mechanical properties and swelling ratios was measured. Significant changes in compressive modulus, tensile modulus, and swelling ratio only occurred for select processed hydrogels. No consistent trends were observed after processing for any of the formulations tested. The effect of storage conditions on cell adhesion and spreading on collagen- and streptococcal collagen-like protein (Scl2-2)-PEG-diacrylamide hydrogels was then evaluated to characterize bioactivity retention after storage. Dry storage conditions preserved bioactivity after 6 weeks of storage; whereas, storage in PBS significantly reduced bioactivity. This loss of bioactivity was attributed to ester hydrolysis of the protein linker, acrylate-PEG-N-hydroxysuccinimide. These studies demonstrate that these processing methods and dry storage conditions may be used to prepare bioactive PEG hydrogel scaffolds with recoverable functionality after storage.