RESUMO
Raw Ca-based montmorillonite (MMT) was treated by H2SO4, calcination and organic compounds (hexadecyltrimethyl ammonium bromide (HTAB), cetylpyridinium chloride (CPC) and chitosan (CTS)), respectively. The modified montmorillonites were characterized by different methods and their adsorption performances for three mycotoxins (Aflatoxin B1 (AFB1), zearalenone (ZEA) and deoxynivalenol (DON)) were evaluated at pH = 2.8 and 8.0, respectively. The results indicate that surfactants (CPC and HTAB) intercalation is the most efficient modification, which obviously improves the adsorption performance of montmorillonite for mycotoxins, with adsorption efficiency of above 90% for AFB1 and ZEA whether under acid or alkaline conditions, due to the increase in basal spacing and the improvement of hydrophobicity. Moreover, the adsorption efficiencies of AFB1 and ZEA over CPC-modified montmorillonite (CPC-AMMT-3) coexisting with vitamin B6 or lysine are still at a high level (all above 94%). All modified montmorillonites, however, have low adsorption efficiency for DON, with somewhat spherical molecular geometry.
Assuntos
Aflatoxina B1/química , Bentonita/química , Inativação Metabólica , Tricotecenos/química , Zearalenona/química , Ácidos/química , Adsorção , Cálcio/química , Micotoxinas/química , TemperaturaRESUMO
A series of modified montmorillonites treated by acid and hexadecyltrimethylammonium bromide (HTAB) were prepared and characterized, and their adsorption performances for three mycotoxins (aflatoxin B1, zearalenone, and deoxynivalenol) were evaluated at pH 2.8 and 8.0, respectively. The results indicate that the layers of raw montmorillonite are exfoliated after acid treatment and more active sites for adsorption of weak polar mycotoxins are exposed. While the intercalation of HTAB leads to an obvious increase of the interlamellar spacing and hydrophobic character of montmorillonite. The HTAB-AMMT-3 modified by acid and HTAB exhibits excellent adsorption capacity towards aflatoxin B1 (AFB1) and zearalenone (ZEA) whether in acidic or alkaline conditions compared with raw montmorillonite (MMT). However, all modified montmorillonites have low adsorption capacity for DON due to its poor planarity preventing it from entering into interfacial layer of montmorillonite.
Assuntos
Aflatoxina B1/isolamento & purificação , Bentonita/química , Cetrimônio/química , Zearalenona/isolamento & purificação , AdsorçãoRESUMO
The polymorphic phase transformation of thermally treated pearl powder was investigated by X-ray diffraction and thermoanalytical techniques. The phase transformation was based on quantification of the calcite content at various temperatures using Rietveld refinement analysis. The results show that the phase transformation of pearl aragonite occurred within a temperature range of 360-410 °C, which is 50-100 °C lower than the range for non-biomineralized aragonite. These thermoanalytical results suggest that the phase transformation of pearl aragonite may occur immediately after the thermal decomposition of the organic matrix in the pearl powder. An important finding is that decomposition of the organic matrix may greatly facilitate such transformation by releasing additional space for an easier structural reconstruction during the phase transformation process.
Assuntos
Carbonato de Cálcio/química , Transição de Fase , Temperatura , Varredura Diferencial de Calorimetria , Modelos Moleculares , Pós , Termogravimetria , Fatores de TempoRESUMO
A new tetragonal phase of PbTiO(3) was discovered, in which each TiO(6) octahedron pair shares an edge and stacks over following pairs in an interlaced manner to form a one-dimensional (1D) columned structure along the c-axis. This new tetragonal phase of PbTiO(3) transforms into a normal perovskite phase in air at elevated temperature.