Waste polyethylene terephthalate plastic derived Zr-MOF for high performance supercapacitor applications.

The chemical conversion of plastic waste into metal-organic framework (MOF) materials has emerged as a significant research field in addressing issues associated to the environment and the economy. The significant advantages of MOFs as electrode material for energy/supercapacitors arises from their extensive surface area and notable porosity. The present study involved the synthesis of Zirconium-Metal Organic Frameworks (Zr-MOF) by the solvothermal method, utilizing plastic waste in the form of Polyethylene terephthalate (PET) bottles. The morphological and structural characteristics of the Zr-MOF were inspected through several analytical techniques, including scanning electron microscopy, transmission electron microscopy, X-ray diffraction, and Fourier-transform infrared spectroscopy analysis. The as prepared Zr-MOF demonstrated very high specific surface area of 927.567 m2 g-1 with mesoporous nature of the materials estimate by BJH method. The electrochemical characteristics of the Zr-MOF in 3-electrode system exhibited a notable specific capacitance of 822 F g-1 when subjected to a low scan rate of 2 mV S-1, while the specific capacitance estimated through galvanostatic charge-discharge exhibited an enhanced value of 890 F g-1 at a current density of 0.5 A g-1. Additionally, the working electrode composed of Zr-MOF demonstrated noteworthy capacitance retention of 92% after 5000 charge discharge cycles. This research presents novel opportunities for the utilization of waste PET bottles in fabrication of highly functional Zr-MOF, aiming to advance the development of next-generation supercapacitors and environmental remediation.

Electrospun Bimetallic NiCr Nanoparticles@Carbon Nanofibers as an Efficient Catalyst for Hydrogen Generation from Ammonia Borane.

In this study, we report on the fabrication and utilization of NiCr alloy nanoparticles (NPs)-decorated carbon nanofibers (CNFs) as efficient and competent non-precious catalysts for the hydrolytic dehydrogenation of ammonia borane (AB) at 25 ± 2 °C. The introduced NFs have been fabricated in one step using a high-temperature thermal decomposition of the prepared electrospun nanofiber mats (nickel acetate tetrahydrate, chromium acetate dimer, and polyvinyl alcohol) in an inert atmosphere. The chemical composition of the NFs with different proportions of Ni1-xCrx (x = 0.0, 0.1, 0.15, 0.2, 0.25, 0.3) was established via standard characterization techniques. These techniques proved the formation of disorder Cr2Ni3 alloy and carbon for all the formulations. The as-synthesized composite NFs exhibited a higher catalytic performance for AB dehydrogenation than that of Cr-free Ni-CNFs. Among all the formulations, the sample composed of 15% Cr shows the best catalytic performance, as more H2 was released in less time. Furthermore, it shows good stability, as it is recyclable with little decline in the catalytic activity after six cycles. It also demonstrates the activation energy, entropy (ΔS), and enthalpy (ΔH) with 37.6 kJ/mole, 0.094 kJ/mole, and 35.03 kJ/mole, respectively. Accordingly, the introduced catalyst has a lower price with higher performance encouraging a practical sustainable H2 energy application from the chemical hydrogen storage materials.