This research is aimed at studying the properties of polymer anticorrosion coatings based on ED-20 resin widely used in practice and industrial wastes. In this work, three basic types of nanoscale nanofillers were chosen: dispersed particles-microsilica, microspheres obtained at Kazakh enterprises, and carbon nanotubes. Physicochemical research methods were used in the research: a laser analyzer for studying the dispersibility of industrial waste and spectrometric research methods. The properties of materials were investigated by standardized methods. The obtained results show that the introduction of microsilica and microspheres obtained at Kazakhstani enterprises, used as additives, improves both the physical and mechanical properties of epoxy composites compared to the standard (control) material. The results of experiments have shown that the optimal content of additives of microsilica and microspheres provides an improvement in the physical and mechanical properties of epoxy composites in comparison with the standard (control) material. Studies have shown that the introduction of microspheres into ED-20 polymer increases impact toughness. The introduction of microsilica into the matrix contributes to the increase of elastic modulus. Experimental studies of optical properties of samples of carbon composite polymer films based on polystyrene (PS) with additives of carbon nanotubes C60 and C70 and multilayer carbon nanotubes were also carried out. The experimental results obtained for the optical properties of polymer composites based on basic polymers from solid waste and carbon nanotubes showed that the optical properties of polymer composites undergo noticeable changes.
RESUMO
An analysis of common reinforcement methods of machine parts and theoretical bases for the selection of their chemical composition were carried out. Prospects for using flux-cored arc welding (FCAW) to restore and increase the wear resistance of machine parts in industries such as metallurgy, agricultural, wood processing, and oil industry were presented. It is noted that conventional series electrodes made of tungsten carbide are expensive, which limits their widespread use in some industries. The scope of this work includes the development of the chemical composition of tungsten-free hardfacing alloys based on the Fe-Mo-B-C system and hardfacing technology and the investigation of the microstructure and the mechanical properties of the developed hardfacing alloys. The composition of the hardfacing alloys was developed by extending the Fe-Mo-B-C system with Ti and Mn. The determination of wear resistance under abrasion and impact-abrasion wear test conditions and the hardness measurement by means of indentation and SEM analysis of the microstructures was completed. The results obtained show that the use of pure metal powders as starting components for electrodes based on the Fe-Mo-B-C system leads to the formation of a wear-resistant phase Fe(Mo,B)2 during FCAW. The addition of Ti and Mn results in a significant increase in abrasion and impact-abrasion wear resistance by 1.2 and 1.3 times, respectively.