Origins and Importance of Intragranular Cracking in Layered Lithium Transition Metal Oxide Cathodes.

Li-ion batteries have a pivotal role in the transition toward electric transportation. Ni-rich layered transition metal oxide (LTMO) cathode materials promise high specific capacity and lower cost but exhibit faster degradation compared with lower Ni alternatives. Here, we employ high-resolution electron microscopy and spectroscopy techniques to investigate the nanoscale origins and impact on performance of intragranular cracking (within primary crystals) in Ni-rich LTMOs. We find that intragranular cracking is widespread in charged specimens early in cycle life but uncommon in discharged samples even after cycling. The distribution of intragranular cracking is highly inhomogeneous. We conclude that intragranular cracking is caused by local stresses that can have several independent sources: neighboring particle anisotropic expansion/contraction, Li- and TM-inhomogeneities at the primary and secondary particle levels, and interfacing of electrochemically active and inactive phases. Our results suggest that intragranular cracks can manifest at different points of life of the cathode and can potentially lead to capacity fade and impedance rise of LTMO cathodes through plane gliding and particle detachment that lead to exposure of additional surfaces to the electrolyte and loss of electrical contact.

Ultra-Small Air-Stable Triplet-Triplet Annihilation Upconversion Nanoparticles for Anti-Stokes Time-Resolved Imaging.

Image contrast is often limited by background autofluorescence in steady-state bioimaging microscopy. Upconversion bioimaging can overcome this by shifting the emission lifetime and wavelength beyond the autofluorescence window. Here we demonstrate the first example of triplet-triplet annihilation upconversion (TTA-UC) based lifetime imaging microscopy. A new class of ultra-small nanoparticle (NP) probes based on TTA-UC chromophores encapsulated in an organic-inorganic host has been synthesised. The NPs exhibit bright UC emission (400-500 nm) in aerated aqueous media with a UC lifetime of ≈1 µs, excellent colloidal stability and little cytotoxicity. Proof-of-concept demonstration of TTA-UC lifetime imaging using these NPs shows that the long-lived anti-Stokes emission is easily discriminable from typical autofluorescence. Moreover, fluctuations in the UC lifetime can be used to map local oxygen diffusion across the subcellular structure. Our TTA-UC NPs are highly promising stains for lifetime imaging microscopy, affording excellent image contrast and potential for oxygen mapping that is ripe for further exploitation.

O3 to O1 Phase Transitions in Highly Delithiated NMC811 at Elevated Temperatures.

Nickel-rich layered oxide cathodes such as NMC811 (LixNi0.8Mn0.1Co0.1O2) currently have the highest practical capacities of cathodes used commercially, approaching 200 mAh/g. Lithium is removed from NMC811 via a solid-solution behavior when delithiated to xLi > 0.10, maintaining the same layered (O3 structure) throughout as observed via operando diffraction measurements. Although it is possible to further delithiate NMC811, it is kinetically challenging, and there are significant side reactions between the electrolyte and cathode surface. Here, small format, NMC811-graphite pouch cells were charged to high voltages at elevated temperatures and held for days to access high states of delithiation. Rietveld refinements on high-resolution diffraction data and indexing of selected area electron diffraction patterns, both acquired ex situ, show that NMC811 undergoes a partial and reversible transition from the O3 to the O1 phase under these conditions. The O1 phase fraction depends not only on the concentration of intercalated lithium but also on the hold temperature and hold time, indicating that the phase transition is kinetically controlled. 1H NMR spectroscopy shows that the proton concentration decreases with O1 phase fraction and is not, therefore, likely to be driving the O3-O1 phase transition.

The influence of electrochemical cycling protocols on capacity loss in nickel-rich lithium-ion batteries.

The transition towards electric vehicles and more sustainable transportation is dependent on lithium-ion battery (LIB) performance. Ni-rich layered transition metal oxides, such as NMC811 (LiNi0.8Mn0.1Co0.1O2), are promising cathode candidates for LIBs due to their higher specific capacity and lower cost compared with lower Ni content materials. However, complex degradation mechanisms inhibit their use. In this work, tailored aging protocols are employed to decouple the effect of electrochemical stimuli on the degradation mechanisms in graphite/NMC811 full cells. Using these protocols, impedance measurements, and differential voltage analysis, the primary drivers for capacity fade and impedance rise are shown to be large state of charge changes combined with high upper cut-off voltage. Focused ion beam-scanning electron microscopy highlights that extensive microscale NMC particle cracking, caused by electrode manufacturing and calendering, is present prior to aging and not immediately detrimental to the gravimetric capacity and impedance. Scanning transmission electron microscopy electron energy loss spectroscopy reveals a correlation between impedance rise and the level of transition metal reduction at the surfaces of aged NMC811. The present study provides insight into the leading causes for LIB performance fading, and highlights the defining role played by the evolving properties of the cathode particle surface layer.

Bulk fatigue induced by surface reconstruction in layered Ni-rich cathodes for Li-ion batteries.

Ni-rich layered cathode materials are among the most promising candidates for high-energy-density Li-ion batteries, yet their degradation mechanisms are still poorly understood. We report a structure-driven degradation mechanism for NMC811 (LiNi0.8Mn0.1Co0.1O2), in which a proportion of the material exhibits a lowered accessible state of charge at the end of charging after repetitive cycling and becomes fatigued. Operando synchrotron long-duration X-ray diffraction enabled by a laser-thinned coin cell shows the emergence and growth in the concentration of this fatigued phase with cycle number. This degradation is structure driven and is not solely due to kinetic limitations or intergranular cracking: no bulk phase transformations, no increase in Li/Ni antisite mixing and no notable changes in the local structure or Li-ion mobility of the bulk are seen in aged NMCs. Instead, we propose that this degradation stems from the high interfacial lattice strain between the reconstructed surface and the bulk layered structure that develops when the latter is at states of charge above a distinct threshold of approximately 75%. This mechanism is expected to be universal in Ni-rich layered cathodes. Our findings provide fundamental insights into strategies to help mitigate this degradation process.

Engineering the nanostructure of a polymer-nanocomposite film containing Ti-based core-shell particles to enhance dielectric response.

Nylon-6 based polymer-nanocomposite (PNC) dielectrics containing nano-regions of Ti-only and Ag + Ti have been manufactured by layer-by-layer deposition. By varying the thickness and deposition rate of individual layers, the PNC structure was manipulated at the nano-scale and then studied using various types of transmission electron microscopy (TEM). Enhanced PNC dielectric properties, with a dielectric constant k as high as ∼73, were shown to relate critically to in situ reactions and the detailed nano-arrangement of the resulting Ti (core)-TiOx (shell) and Ag nanoparticles.

Core-shell nanoparticles and enhanced polarization in polymer based nanocomposite dielectrics.

We present a detailed study of the evolution and nature of metallic core-oxide shell particles and the role of nanostructure in the physics of enhanced polarization in polymer-nanocomposite (PNC) based dielectrics. Nylon-6 based PNCs consisting of aluminium (core)-aluminium oxide (shell) nanoparticles were fabricated by a vacuum deposition technique. Their resulting high polarizability was closely related to the formation and chemistry of the core-shell structure that was revealed by transmission electron microscopy to comprise a highly-defective, strained and non-stoichiometric semi-crystalline/amorphous Al-oxide shell.