The manufacture, optical properties, and mechanical aspects of europium-doped borate glasses.

An investigation into the optical and mechanical properties of a novel borate glasses with the chemical composition of 70 B2O3-10 Li2O-10ZnO-5Bi2O3-5CaO-xEu2O3 was conducted. The glassy specimens of Eu3+-doped borate were prepared by the melting-quenching technique. An enhanced density from 3.0860 to 3.2176 g cm-3 and reduced molar volume from 29.27819 to 29.17447 (cm3 mol-1) are the outcome of increasing the concentration of Eu3+ in glasses. Plotting the extinction coefficient, dielectric constant (ε1, ε2), and refractive index (n) against wavelength reveals that they all rise as level of Eu3+ elements in the glass lattice increases. An increase in Eu3+ concentration results in a decrease in both the volume (VELF) and surface (SELF) energy loss functions. Also, all elastic-mechanical moduli (such as Young's, Bulk, Shear, and Elongation) increase with increasing the quantity of Eu3+ ions in the glass lattice. The Young's modulus (Y, GPa) of the glassy specimens was 34.512, 36.089, 36.504, 36.730 and 37.114 GPa for x equal 0, 0.25, 0.5, 0.75 and 1 mol ratio in the glass system, and coded by Eu-0.0, Eu-0.25, Eu-0.5, Eu-0.75 and Eu-1.0, respectively. Growing Eu2O3 levels resulted in an increase in Micro-Hardness from 2.050 to 2.146 GPa. Poisson's ratio values for Eu-0.0, Eu-0.250, Eu-0.5, Eu-0.75 and Eu-1.0 were 0.273, 0.275, 0.277, 0.277 and 0.278, respectively.

Parasitism by the endoparasitoid, Cotesia flavipes induces cellular immunosuppression and enhances susceptibility of the sugar cane borer, Diatraea saccharalis to Bacillus thuringiensis.

Cotesia flavipes Cameron (Hymenoptera: Braconidae), is a gregarious larval endoparasitoid of the sugarcane borer, Diatraea saccharalis Fabricius (Lepidoptera: Crambidae). The aim of this research was to analyze cellular immunosuppression of D. saccharalis parasitized by C. flavipes in terms of encapsulation, melanization, and hemocyte nodule formation. The encapsulation assay was done 1 and 6 days after parasitoid oviposition. In addition, the susceptibility of parasitized and nonparasitzed larvae to Bacillus thuringiensis HD 73 strain was assessed. 3, 12, and 24 h after bead injection; the percentages of encapsulation were significantly higher in unparasitized larvae compared to larvae parasitized 1 and 6 days after oviposition. Interestingly, there was a significant reduction in numbers of beads encapsulated at 1 day after oviposition compared to 6 days, and unparasitized larvae. The percentage of melanized beads decreased significantly in parasitized larvae compared to control. There was a reduction in the number of nodules in parasitized larvae compared to unparasitized controls. Larvae that were injected with polyndavirus 24 h before beads were injected showed significantly reduced encapsulation responses relative to control larvae. The D. saccharalis parasitized by C. flavipes exhibited higher susceptibility to B. thuringiensis. These results suggest that parasitization induced host immunosuppression, and the immunosuppression factors could impair the defense capacity against microbial pathogens--causing an increase in pathogen susceptibility.