A rubberized impact absorbing pavement can reduce the head injury risk in vulnerable road users: A bicycle and a pedestrian accident case study.

OBJECTIVE: Vulnerable Road Users (VRU), including pedestrians and cyclists, are generally the least protected road users and are frequently missed in the planning process of preventive measures. Rubberized asphalt mixtures were originally developed as a possible environmentally friendly solution to recycle the End-of-Life Tires while making the pavements more durable. The objective of the current study was to explore the effects of increasing the rubber content of the common rubberized asphalt mixtures in reducing the head injuries risk for VRUs. METHOD: To achieve this purpose, four different sample series with 0, 14, 28, and 33 weight percent rubber in each were tested. A compressive test without permanent deformation and one with failure were performed on each sample series. The mechanical behavior of each set was modeled using a MAT_SIMPLIFIED_RUBBER material model in LS-Dyna and validated against a standard Head Injury Criterion (HIC) drop test. Ultimately, previously low-speed accident reconstructed cases, a bicycle and a pedestrian one, were used to assess the effect of varying the rubber content on reducing the head injury risk. RESULTS: In the bicycle accident case, the risk of skull fracture was reduced from 0.99 to 0.29 when comparing the non-rubberized asphalt mixture with the 33% rubber mixture. In the same accident case, the risk of concussion, evaluated using the logistic regression method, was reduced from 0.97 in the non-rubberized mixture to 0.81 in the 33% rubber mixture. The initial conditions, linear and rotational velocities, were lower for the pedestrian case compared to the bicycle case (the bicycle case was more severe compared to the pedestrian case), which led to lower strains in the pedestrian case. In the pedestrian accident case, the risk of skull fracture was reduced from 1.00 in the non-rubberized mixture to 0.63 in the 33% rubber mixture, while the risk of concussion was reduced from 0.64 to 0.07. CONCLUSION: The rubberized asphalt mixtures could reduce the head injury risk for the studied cases when the rubber content in the asphalt mixture increases.

Influence of Freeze-Thaw Cycles on the Mechanical Properties of Highly Rubberised Asphalt Mixtures Made with Warm and Cold Asphalt Binders.

The present study has been developed to investigate the effect of freeze and thaw (F-T) cycles on the characteristics of highly rubberised asphalt materials to be used as impact-absorbing pavement (IAP) in urban road infrastructures. The tested samples were produced in the laboratory following the dry process incorporation. Two main types of crumb rubber particles in the range of 0-4 mm were used. Moreover, two types of binders, one warm and one cold, were utilised to prove the feasibility of cold-produced admixtures. The temperature range of the F-T procedure was comprised between -18 ± 2 °C (dry freezing), and 4 ± 2 °C (in water), and the cycles were repeated, on the samples, 10 times. At 0, 1, 5, and 10 cycles, the samples were tested with non-destructive and destructive testing methods, including air voids content, ITSM, ITS, and Cantabro loss. The waters of the thawing period were collected, and the pH, electric conductivity, and particle loss were measured. A consequent change in mechanical behaviour has been recorded between warm and cold produced samples. However, the tests found that the F-T cycles had limited influence on the deterioration of the highly rubberised samples. The loss of particles in the thaw waters were identified as being potentially caused by the temperature stresses. The research suggested various ways to optimise the material to enhance the cold-produced layer mechanical performances, aiming at a fume and smell-free industrialised solution and reducing the potential leaching and particle losses.

Leaching of PAHs from rubber modified asphalt pavements.

The present study aimed to, for the first time, quantify the total content of 16 priority EPA PAHs in end-of-life tyre derived crumb rubber granulates and various manufactured rubberised asphalt mix designs. After identifying the availability of 16 EPA PAHs, the leaching behaviour of rubberised asphalt specimens, were evaluated using the Dynamic Surface Leaching Test (DSLT) based on CEN/TS 16637-2:2014 standard. This was prior to modelling the release mechanisms of PAHs by utilizing a mathematical diffusion-controlled leaching model. According to the results, the total content of 16 EPA PAHs in crumb rubber granulates ranged between 0.061 and 8.322 µg/g, which were associated with acenaphthene and pyrene, respectively. The total content of PAHs in rubberised asphalt specimens varied between 0.019 and 4.992 µg/g depending on the volume of crumb rubber granulates in the asphalt concrete mix design, and type of binder. Results of the leaching experiments revealed that the highest leached PAHs were benzo[b]fluoranthene, benzo[k]fluoranthene and naphthalene with a 64-days cumulative release per specimen surface area > 1 µg/m2. Acenaphthylene, fluoranthene, fluorene and indeno[1,2,3-c,d]pyrene were released in cumulative concentrations between 0.1 and 1 µg/m2. The PAHs with a cumulative release potential below 0.1 µg/m2 during DSLT were benzo[a]anthracene, benzo[a]pyrene, benzo[g,h,i]perylene and chrysene. The diffusion coefficients, which were calculated by mathematical modelling of DSLT data, revealed that the leaching process of 16 EPA PAHs from surface of rubberised asphalt concrete mix designs fitted all the criteria set by the NEN 7345 standard for diffusion-controlled leaching during all stages of leaching experiments.