pH-sensitive semi-interpenetrating network of microcrystalline cellulose and methacrylic acid hydrogel for the oral delivery of insulin.

Insulin is commonly administered to diabetic patients subcutaneously and has shown poor patient compliance. Due to this, research has been carried out extensively to find molecules that could deliver insulin orally. In this context, a new type of pH-responsive hydrogel, composed of microcrystalline cellulose and methacrylic acid-based hydrogels, has been developed and studied for the oral delivery of insulin. These hydrogels were prepared by free radical polymerization using potassium persulphate as initiator and N, N'-methylenebisacrylamide as a cross-linker. These pH-sensitive hydrogels showed swelling in distilled water as high as 5800 %. The hydrogels were investigated for swelling in saline and glucose solutions, and pH sensitivity was confirmed by swelling in solutions of different pH. The morphological shape was established by SEM, and the structure was analyzed by FTIR. Thermal degradation was investigated by TGA. In vitro release studies have confirmed pH sensitivity, showing lower insulin release at pH 1.2 than at pH 6.8. The encapsulation efficiency was determined to be 56.00 ±â€¯0.04 %. It was further validated by in-vivo investigations for which insulin was loaded into hydrogels and administered orally to healthy and diabetic Wistar rats at 40 IU/kg, showing maximum hypoglycemic effect at 6 h, which was sustained for 24 h. In the stomach's acidic environment, the gels remained unaffected due to the formation of intermolecular polymer complexes. Insulin remained in the gel and was protected from proteolytic degradation. Thus, pH-responsive methacrylic acid-based hydrogels are promising for biomedical applications, especially oral drug delivery.