Synergistic effects of sodium ascorbate and acetone to restore compromised bond strength after enamel bleaching.

AIM: To evaluate the effect of a new experimental solution containing sodium ascorbate (SA) and acetone on reversing compromised bonding to enamel immediately after bleaching. MATERIALS AND METHODS: The buccal surface of intact, extracted human premolars (n = 60) was bleached. The teeth were then randomly assigned to 6 groups according to the type of pretreatment applied prior to adhesive procedures: 10% SA in acetone-water solution applied for 1 and 5 min (groups 1 and 2, respectively); aqueous solution of 10% SA applied for 10 min (group 3); 100% acetone applied for 10 min (group 4); no pretreatment (negative control; group 5). An additional group (positive control; group 6) comprised unbleached teeth (n = 12). Two composite microcylinders were bonded on each specimen for evaluation of microshear bond strength (MBS) and failure modes. Data were analyzed using the one-way ANOVA and Tukey's post-hoc and chi-square tests at P = 0.05. RESULTS: Groups 1 and 2 yielded similar MBS values to groups 4 and 6 (positive control). The mean MBS of groups 3 and 5 (negative control) were similar, and significantly lower than that of the positive control group. CONCLUSION: The application of 10% SA in an acetone-water solution prior to bonding procedures can restore compromised enamel bond strength to its unbleached state within a clinically acceptable time of 1 min.

Shear bond strength of orthodontic color-change adhesives with different light-curing times.

BACKGROUND: The purpose of this study was to evaluate the effect of light-curing time on the shear bond strength (SBS) of two orthodontic color-change adhesives (CCAs). MATERIALS AND METHODS: A total of 72 extracted premolars were randomly assigned into 6 groups of 12 teeth each. Subsequent to primer application, a metal bracket was bonded to the buccal surface using an orthodontic adhesive. Two CCAs (Greengloo and Transbond Plus) were tested and one conventional light-cured adhesive (Resilience) served as control. For each adhesive, the specimens were light-cured for two different times of 20 and 40 s. All the specimens underwent mechanical testing using a universal testing machine to measure the SBS. Adhesive remnant index (ARI) was used to assess the remnant adhesive material on the tooth surface. All statistical analyses were performed using SPSS software. The significance level for all statistical tests was set at P ≤ 0.05. RESULTS: The SBSs of the tested groups were in the range of 14.05-31.25 MPa. Greengloo adhesive showed the highest SBS values when light-cured for 40 s, and Transbond Plus adhesive showed the lowest values when light-cured for 20 s. ARI scores of Transbond Plus adhesive were significantly higher than those of controls, while other differences in ARI values were not significant. CONCLUSION: Within the limitations of his study, decreasing the light-curing time from 40 to 20 s decreased the SBS of the tested adhesives; however, this decline in SBS was statistically significant only in Transbond Plus adhesive.

The effect of photoactivation time and light tip distance on the degree of conversion of light and dual-cured dentin adhesives.

BACKGROUND: The degree of conversion of dental adhesive is an important parameter since poor mechanical properties are related to low percentage of monomer-to-polymer conversion within resin-based materials. OBJECTIVES: To evaluate the influence of polymerization time and light guide distance on the degree of conversion (DC) of three contemporary dental adhesives. MATERIALS AND METHODS: The spectral data of ExciTE DSC, Single Bond ® , and Adper ® Prompt L-Pop were analyzed using FTIR spectroscopy after 20 s, 40 s, and 60 s of photoactivation times. Light tip distances were kept at 1, 3, and 6 mm during the exposures. STATISTICS: Data were analyzed using ANOVA and Tukey's test (α = 0.05). RESULTS: Within groups, greater DC values were found using a tip distance of 1 mm or a 60-s curing time for Single Bond ® (59%) and Adper ® Prompt L-Pop (65%). No statistically significant difference (P > 0.05) was found using either 1 mm or 3 mm tip distances after 20 s, 40 s, and 60 s of light curing time for Single Bond ® . ExciTE ® DSC showed the greatest DC values with light tip distances of 1 mm (90%) and 3 mm (89%), using 60 s of light curing. CONCLUSION: The self-etch adhesive Adper ® Prompt L-Pop could be applied in shallow cavity preparations and must be light cured for at least 40 s. The light-cured total-etch adhesive ExciTE ® DSC could be applied in every restorative scenario if the curing time is extended up to 60 s or if the tip distance is extended up to 3 mm.