RESUMO
The properties of oxide dispersion-strengthened steels are highly dependent on the nature and size distribution of their constituting nano-oxide precipitates. A fine control of the processes of synthesis would enable the optimization of pertinent properties for use in various energy systems. This control, however, requires knowledge of the precise mechanisms of nucleation and growth of the nanoprecipitates, which are still a matter of debate. In the present study, nano-oxide precipitates were produced via the implantation of Y, Ti, and O ions in two different sequential orders in an Fe-10%Cr matrix that was subsequently thermally annealed. The results show that the oxides that precipitate are not necessarily favoured thermodynamically, but rather result from complex kinetics aspects related to the interaction between the implanted elements and induced defects. When Y is implanted first, the formation of nanoprecipitates with characteristics similar to those in conventionally produced ODS steels, especially with a core/shell structure, is evidenced. In contrast, when implantation starts with Ti, the precipitation of yttria during subsequent high-temperature annealing is totally suppressed, and corundum Cr2O3 precipitates instead. Moreover, the systematic involvement of {110} matrix planes in orientation relationships with the precipitates, independently of the precipitate nature, suggests matrix restriction effects on the early stages of precipitation.
RESUMO
As an important metal three-dimensional printing technology, electron beam melting (EBM) is gaining increasing attention due to its huge potential applications in aerospace and biomedical fields. EBM processing of Ti-6Al-4V as well as its microstructure and mechanical properties were extensively investigated. However, it is still lack of quantitative studies regarding its microstructural evolution, indicative of EBM thermal process. Here, we report α' martensitic transformation and α/ß interface evolution in varied printing thicknesses of EBM-printed Ti-6Al-4V block samples by means of atom probe tomography. Quantitative chemical composition analysis suggests a general phase transformation sequence. By increasing in-fill hatched thickness, elemental partitioning ratios arise and ß volume fraction is increased. Furthermore, we observe kinetic vanadium segregation and aluminum depletion at interface front and the resultant α/ß interface widening phenomenon. It may give rise to an increased α/ß lattice mismatch and weakened α/ß interfaces, which could account for the degraded strength as printing thickness increases.
RESUMO
The Stranski-Krastanov growth of Ge islands on Si(001) has been widely studied. The morphology changes of Ge islands during growth, from nucleation to hut/island formation and growth, followed by hut-to-dome island transformation and dislocation nucleation of domes, have been well described, even at the atomic scale, using techniques such as scanning tunneling microscopy and transmission electron microscopy. Although it is known that these islands do not consist of pure Ge (due to Si/Ge intermixing), the composition of the Ge islands is not precisely known. In the present work, atom probe tomography was used to study the composition of buried dome islands at the atomic scale, in the three-dimensional space. The core of the island was shown to contain about 55 atom % Ge, while the Ge composition surrounding this core decreases rapidly in all directions in the islands to reach a Ge concentration of about 15 atom %. The Ge distribution in the islands follows a cylindrical symmetry and Ge segregation is observed only in the {113} facets of the islands. The Ge composition of the wetting layer is not homogeneous, varying from 5 to 30 atom %.