In vitro evaluation of the antimicrobial effects of different intracanal medications in necrotic immature teeth.

AIM: This was to assess the antimicrobial effectiveness of pastes used as intracanal medicaments against Enterococcus faecalis in necrotic immature teeth. METHOD: An agar-disc diffusion method over a period of 30 days was used. The following medications were analysed: triple antibiotic paste (TAP) I; double antibiotic paste (DAP) I; DAP I with calcium hydroxide; calcium hydroxide paste with saline solution 0.9 %; calcium hydroxide paste with chlorhexidine 2 % gel; DAP II; DAP II with zinc oxide; DAP II with calcium hydroxide; and saline solution 0.9 % as control. The diameters of the halos of inhibition (in mm) of tested medicaments were determined and analysed with one-way analysis of variance and Tukey's post hoc tests. RESULTS: TAP I (G1) was significantly more effective against E. faecalis, and showed the largest halo of inhibition during all the experiments. DAP groups (G2 and G6) also showed inhibiting bacterial growth with said inhibition remaining stable throughout the 30-day period. In contrast, G4 and G5 groups, in which Ca(OH)2 was added to saline and chlorhexidine, had no antibacterial effect. CONCLUSIONS: TAP and DAP showed better antibacterial efficacy and remained active for 30 days. Combination of Ca(OH)2 with antibiotics should be avoided, due to the possibility of antibiotic hydrolysis.

Degradation of trans-polyisoprene after root filling with thermoplasticized techniques.

AIM: To evaluate ex vivo degradation of gutta-percha following six thermoplastic obturation techniques. METHODOLOGY: Ninety human-extracted mandibular premolars were selected and divided randomly into nine groups for filling. Group 1: thermomechanical compaction for 3 s with Konne gutta-percha points (Konne Ind. e Com. de Mat. Odontol., Belo Horizonte, MG, Brazil); Group 2: thermomechanical compaction for 3 s with Dentsply TP gutta-percha points (Dentsply Indústria e Comércio Ltda, Petrópolis, R.J. Brazil); Group 3: thermomechanical compaction for 10 s with Konne; Group 4: thermomechanical compaction for 10 s with Dentsply TP; Group 5: warm vertical condensation using System B (EIE/Analytic, Richmond, WA, USA) with Konne; Group 6: warm vertical condensation using System B with Dentsply TP; Group 7: vertical condensation with Konne; Group 8: vertical condensation with Dentsply TP; Group 9: Microseal cone (Analytic Endodontics, Glendora, CA, USA). A further four groups were assessed without using teeth, Group 10: Microseal microflow (Analytic Endodontics); Group 11: Obtura (Obtura Corporation, Penton, MO, USA); Group 12: Obtura flow (Obtura Corporation); Group 13: Thermafil (Dentsply Maillefer, Tulsa, OK, USA). The filling material was removed from the root canal and trans-1,4-polyisoprene isolated by solubilization of the root filling remnants in chloroform followed by filtration and centrifugation. By gel permeation chromatography and infrared spectroscopy, the occurrence and degree of degradation were assessed. The results were analysed statistically using the Kruskal-Wallis test. With differential scanning calorimetry, the thermal behaviour of the gutta-percha was determined. RESULTS: A significant decrease in polymer molar mass and the production of carboxyl and hydroxyl groups in the polymer were observed with thermomechanical compaction used for 10 s and vertical condensation filling techniques (P = 0.0001 and P = 0.0005, respectively). Other techniques caused no polymer degradation. CONCLUSION: Polyisoprene degrades with high temperature. Thermomechanical compaction for 10 s and vertical condensation were associated with the greatest degradative process.

A case of unusual anatomy in second mandibular molar with four canals.

Success in root canal treatment is achieved after thought cleaning and shaping followed by the complete obturation of root canal system. Such treatment may be performed in root canal systems that do not comply with the normal anatomical features described in standard textbooks. This article describes the conventional root canal treatment on an unusual mandibular second molar with four root-canals.

Comparison of the percentage of gutta-percha-filled area obtained by Thermafil and System B.

The aim of this study was to determine the percentage of gutta-percha-filled area (GPFA) obtained by Thermafil and System B techniques using light microscopy and digital image processing. Forty-five human mandibular first molars were prepared and obturated as follows: Group 1: lateral condensation (n = 15); Group 2: System B (n = 15); and Group 3: Thermafil system (n = 15). Horizontal sections were cut 4 and 6 mm from the apical foramen of each tooth. The samples were metallographically prepared and taken through photomicrographs. Using digital analysis, the cross-sectional area of the canal and the gutta-percha areas were measured. The GPFA data obtained for the three groups were analysed using the non-parametric Friedman and Wilcoxon Signed-Ranks tests. Significant differences were found between Group 3 and Group 2-Group 1. No significant difference was found between Group 2 and Group 1. The Thermafil system produced significantly higher GPFAs than lateral condensation and System B techniques (P < 0.01). This result suggests that the Thermafil system can reduce sealer and voids.

Degradation of trans-polyisoprene over time following the analysis of root fillings removed during conventional retreatment.

AIM: To evaluate in vivo degradation of root filling materials over time. METHODOLOGY: Thirty-six root filled teeth with or without periapical lesions were selected. Teeth with poor coronal restoration were not included. The teeth had been root filled 3-30 years previous and were scheduled for conventional retreatment. The association of root canal treatment, age, periapical lesion and root filling degradation was investigated. The filling material was removed from the root canal using files and no solvent. Trans-1,4-polyisoprene was isolated through solubilization of root filling remnants in chloroform followed by filtration and centrifugation. Gel permeation chromatography (GPC) and infrared spectroscopy (FT-IR) were utilized to study the occurrence and degree of degradation. The GPC and FT-IR data were collected for each sample and analysed statistically using the Kruskal-Wallis test. RESULTS: Degradation of trans-1,4-polyisoprene was a slow process. The process was identified as an oxidation reaction through the production of carboxyl and hydroxyl groups. Compared with the control group, significant molar mass decrease was noted after 15 years (P = 0.0146) in teeth with no periapical lesions. However, in teeth associated with periapical lesions the number of years for significant degradation was reduced to 5 (P = 0.0009). CONCLUSION: Polyisoprene degrades inside root canals as an oxidative process. The presence of periapical lesions was associated with a more rapid onset of degradation.